Addressing Unfavorable Influence of Particle Cracking with a Strengthened Shell Layer in Ni-Rich Cathodes

Meng Liu,Zhongming Ren,Deyu Wang,Haitao Zhang,Yujing Bi,Cai Shen,Bingkun Guo

DOI: https://doi.org/10.1021/acsami.1c05535

2021-04-15

Abstract:Ni-rich layered materials are widely accepted as pivotal cathode materials to realize low-cost high-energy-density batteries. However, they still suffer from the intrinsic mechanically induced degradation due to the large lattice deformation. Here, we fabricate a strengthened shell layer on polycrystalline secondary particles to address the unfavorable influence of particle cracking instead of suppressing their bulky pulverization. This tough layer, constructed via welding LiNi_0.8Co_0.1Mn_0.1O₂ primary particles with a Nb-based ceramic, increases Young's modulus of the particles 2.6 times. This layer allows the particles work properly with the intact spherical morphology even after bulk cracking. It seems that this tough skin stops the bulky flaws growing into perforated fissures and keeps the electrodes from quick polarization. This approach demonstrates that, besides addressing the intrinsic challenges directly, appropriate particle engineering is another efficient way to exploit the potentials of Ni-rich cathodes and power batteries made out of them.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c05535?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c05535</a>.SEM images and EDS mapping, in situ XRD patterns, TEM image and SAED, CV test, voltage profiles, full-cell test, and EIS spectra (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05535/suppl_file/am1c05535_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

This paper attempts to solve the problem of particle cracking in nickel - based lithium - rich layered cathode materials during the charging and discharging process due to mechanical stress. Specifically, although nickel - based lithium - rich materials (such as LiNi\(_{0.8}\)Co\(_{0.1}\)Mn\(_{0.1}\)O\(_2\)) have the advantages of high specific energy and low cost, they are prone to severe lattice deformation during cycling, which leads to mechanical degradation and ultimately results in a decline in battery performance.

### Core problems of the paper

1. **Mechanically - induced particle cracking**: During high - voltage charging and discharging, significant lattice expansion and contraction will occur inside the nickel - based lithium - rich materials, generating anisotropic stress and leading to particle cracking and pulverization. This mechanical failure is one of the main degradation mechanisms of nickel - based lithium - rich cathode materials.

2. **Electrolyte penetration and side reactions**: After particle cracking, the newly generated surface will react with the penetrating electrolyte, consuming Li⁺ ions and forming a new interface layer, increasing the interface resistance and further reducing the cycling stability of the battery.

### Solutions

To solve the above problems, the author proposes a method of constructing a reinforced shell layer by welding Nb - based ceramics to enhance the mechanical properties of secondary particles. Specifically:

- **Construction of the reinforced shell layer**: By welding LiNi\(_{0.8}\)Co\(_{0.1}\)Mn\(_{0.1}\)O\(_2\) primary particles together with Nb - based ceramics, a shell layer with higher strength is formed. The experimental results show that this shell layer increases the Young's modulus of the particles by 2.6 times.

- **Inhibition of crack propagation**: The reinforced shell layer can prevent large - scale defects from expanding into penetrating cracks, maintain the integrity of the particles, and prevent electrolyte penetration and related side reactions from occurring.

- **Improvement of electrochemical performance**: After 200 cycles, the capacity retention rate of the sample with a protective layer is as high as 93.9%, while that of the untreated sample is only 77.2%. This indicates that the reinforced shell layer significantly improves the cycling stability and mechanical durability of nickel - based lithium - rich cathode materials.

### Conclusion

By introducing the reinforced shell layer welded with Nb - based ceramics, the author has successfully solved the problem of particle cracking in nickel - based lithium - rich cathode materials during high - voltage cycling due to mechanical stress. This method not only improves the mechanical strength of the material but also effectively inhibits electrolyte penetration, thereby significantly enhancing the cycling life and performance of the battery.