3D flower-like CuO@PEG composite phase change materials with photo response for applications in energy conversion and storage

Hongdi Pang,Guohui Li,Liqing Cheng,Chuan He,Xiaomei Wang,Xu Zhang

DOI: https://doi.org/10.1016/j.est.2024.110537

IF: 9.4

2024-01-21

Journal of Energy Storage

Abstract:Phase change materials (PCMs) are widely favored because of their high latent heat and considerable potential for thermal storage . However, poor photothermal conversion and limited thermal conductivity capability severely limit their potential in a variety of applications. Herein, polyethylene glycol (PEG) was loaded into three-dimensional (3D) flower-like CuO with high thermal conductivity, and therefore endowed with the functionalities of converting light into heat energy and storing the heat energy. Firstly, high-quality 3D flower-like nano CuO was prepared by a straightforward chemical precipitation method at a lower temperature (80 °C) without the use of surfactants. Then, the 3D flower-like CuO-100 with a large loading space was used to load PEG as much as possible by vacuum impregnation to prepare a high thermal conductivity light-driven CuO-100@PEG-80 composite PCM. DSC results show that the prepared CuO-100@PEG-80 composite PCM has ideal melting enthalpy (159.7 J/g) and crystallization enthalpy (142.7 J/g), and the thermal conductivity of the composite reaches 0.52 W·m −1 ·K −1 . The thermal cycle test and thermogravimetric analysis show that the CuO-100@PEG-80 composite PCM has excellent photo-thermal conversion ability and thermal stability. The photo-thermal conversion efficiency reaches 91.6 % under irradiation intensity of 150 mW/cm 2 and can still remain stable after 50 simulated light on/off cycles. It indicates that CuO-100@PEG-80 possesses significant potential for application in the fields of thermal energy storage and solar energy utilization.

energy & fuels