Abstract:Abstract Mesoporous silica (MS) was prepared through a simple self‐assembly procedure under alkaline condition with tetraethyl orthosilicate (TEOS) as SiO 2 precursor and cetyltrimethyl ammonium bromide (CTAB) as the template. A series of shape‐stabilized composite phase change materials (ss‐CPCMs), using polyethylene glycol 6000 (PEG6000) as the PCM and MS as the matrix with different mass percentage of PEG6000 loadings, was prepared through a vacuum impregnation method. N 2 adsorption‐desorption analyzer measurement showed the specific surface area and average pore size of the as‐prepared porous silica were determined to be 760 m 2 /g and about 3 nm, respectively. Differential scanning calorimetry (DSC) measurements indicated that the melting peak temperatures and latent heats of melting of the composites are varied from 52.3°C to 62.6°C and 32.9 to 186.4 J/g (PEG6000 mass fractions: 0%‐80%), which was proportional to PEG6000 content. Fourier‐transform infrared (FT‐IR) spectroscopy results implied that only the physical interaction existed between the PEG6000 and SiO 2 matrix. The shape‐stability measurements suggested the composite with the 70% mass loading of PEG6000 can still maintained the original shape and no leakage were observed above the much higher melting temperature of PEG6000 (105°C). Thermal cycling test showed that the ss‐CPCM had good thermal reliability and chemical stability although it was experienced 500 melting and cooling cycles. Moreover, the thermal decomposition temperature of the composites (393.2°C) was much larger than the melting temperature of pure PEG6000 (62.6°C), which indicated that composite presented excellent thermal stabilities and was suitable for thermal energy storage applications.

Using surface-modified UiO-66 with hierarchical pores to pack polyethylene glycol for phase change thermal energy storage: Experiment and molecular dynamics simulations

Polyethylene glycol phase change material embedded in a hierarchical porous carbon with superior thermal storage capacity and excellent stability

A novel enhancement of shape/thermal stability and energy-storage capacity of phase change materials through the formation of composites with 3D porous (3,6)-connected metal–organic framework

Using mesoporous carbon to pack polyethylene glycol as a shape-stabilized phase change material with excellent energy storage capacity and thermal conductivity

Polyethylene glycol/silica (PEG@SiO2) composite inspired by the synthesis of mesoporous materials as shape-stabilized phase change material for energy storage

A structured phase change material integrated by MXene/AgNWs modified dual-network and polyethylene glycol for energy storage and thermal management

Thermal characteristics of the multilayered structural MOF-EG/OC composite phase change material in thermal energy storage

Composited phase change material with hierarchical metal foam for efficient thermal energy management

Thermal energy storage performance of hierarchical porous kaolinite geopolymer based shape-stabilized composite phase change materials

Preparation and Thermal Properties of Propyl Palmitate-Based Phase Change Composites with Enhanced Thermal Conductivity for Thermal Energy Storage

Sandwich Fibrous PEG Encapsulations for Thermal Energy Storage

Novel PEG/SiO2/SiO2–modified expanded graphite composite phase change materials for enhanced thermal energy storage performance

Synergistic phase change and heat conduction of low melting-point alloy microparticle additives in expanded graphite shape-stabilized organic phase change materials

Thermal properties of three-dimensional hierarchical porous graphene foam-carbon nanotube hybrid structure composites with phase change materials

Design of a graphene oxide@melamine foam/polyaniline@erythritol composite phase change material for thermal energy storage

Polyethylene glycol/carboxymethyl cellulose/montmorillonite composite phase change materials for thermal management

A polyethylene glycol-based form-stable phase change material supported by nanoarray-modified metal foam

Preparation and thermal properties of shape‐stabilized polyethylene glycol/mesoporous silica composite phase change materials for thermal energy storage

MXene-decorated bio-based porous carbon composite phase change material for superior solar-thermal energy storage and thermal management of electronic components

Mica-stabilized polyethylene glycol composite phase change materials for thermal energy storage

Ti3C2Tx@Polyvinyl alcohol foam-Supported Phase Change Materials with Simultaneous Enhanced Thermal Conductivity and Solar-Thermal Conversion Performance