Abstract:Y zeolite has been regarded as an effective adsorbent in removal of volatile organic compounds (VOCs). However, the low Si/Al ratio causes Y zeolite to preferentially adsorb water when dealing with wet VOCs, which limits its practical application. In present work, Y zeolite was first dealuminated treated by steaming and acid etching, and then the obtained deAlY was used as cores to prepare deAlY@nSiO2 core–shell composites. The shell layer thickness in the as-prepared core–shell composites was adjusted by controlling the hydrolysis of tetraethoxysilane (TEOS). The Si-species yielded from the hydrolysis of TEOS not only fabricated the mesopore shell directed by CTA+, but also entered the zeolite framework by polycondensation with the adjacent hydroxyl (silicon hydroxyl of (SiO)3Si(OH) species or aluminum hydroxyl of penta-coordinated aluminum caused by steaming and acid etching) in the defect sites of the core deAlY. During the adsorption of dry toluene, the as-synthesized composite displayed an adsorption capacity superior to mesopore SiO2 while inferior to deAlY. When toluene and water molecules competed for the adsorption sites, the core–shell composite preferred to adsorb the former because of the greatly reduced sensitivity to the presence of water vapor. Under 55 % and 83 % relative humidity, the core–shell deAlY@nSiO2 (n < 1.5) respectively had 4.2 and 9.0 times higher toluene adsorption than the deAlY. The mesopores in the SiO2 shell was conducive to a fast mass transfer, the high hydrophobic surfaces (internal and external) resulted from reduced hydroxyl content, elevated framework Si/Al ratio and constructed SiO2 shell, contributed to shielding water, which promoted toluene in the wet VOCs to be adsorbed efficiently by the deAlY zeolite core.

The role of layered double hydroxides shell in enhancing the adsorption capacity of NaY zeolite for toluene in wet conditions

Prepared hydrophobic Y zeolite for adsorbing toluene in humid environment

Core-shell deAlY@SiO2 composite: A superior adsorbent for toluene capture under humidity condition

Enhancing Adsorption Capacities of Low-Concentration VOCs under Humid Conditions Using NaY@meso-SiO2 Core–shell Composite

Continuous Synthesis of Mesoporous Y Zeolites from Normal Inorganic Aluminosilicates and Their High Adsorption Capacity for Dibenzothiophene (DBT) and 4,6-Dimethyldibenzothiophene (4,6-DMDBT)

Hierarchical structure ZSM-5/SBA-15 composite with improved hydrophobicity for adsorption-desorption behavior of toluene

Dual-alkali treatment of Y-type zeolite synthesized from lithium-silicon powder waste for enhanced adsorption removal of low-concentration toluene

Enhanced Toluene Adsorption/desorption Dynamic Performances over Modified USY Zeolites after an Aqueous Ammonia Treatment.

Synthesis of Hierarchical LTA Zeolite Membranes by Vapor Phase Transformation

Influence of the surfactant on structural characterizations and molecular adsorption properties of surfactant-templated NaY zeolite

The Design of Core–shell ZSM-5@NiAl-LDH Composites for Efficient Adsorption of VOCs under High Humidity

Enhanced hydrophobic ZSM-5 with high capacity for toluene capture under high-humidity conditions

Attenuating Toluene Mobility In Loess Soil Modified With Anion-Cation Surfactants

Unveiling the Role of Hydrophobicity on Multilayer Carbon Nanosheets Enriched in sp2-Carbon for Toluene Adsorption under Humid Conditions

Adsorptive removal of toluene and dichloromethane from humid exhaust on MFI, BEA and FAU zeolites: An experimental and theoretical study

Pore size control of NaY zeolite by chemical liquid deposition and shape-selective separation

Synthesis and VOCs adsorption properties of Diatomite/FAU-type zeolite composites

Adsorptive properties in toluene removal over hierarchical zeolites

Engineering surface functional groups on mesoporous silica: towards a humidity-resistant hydrophobic adsorbent

Modified Silica Adsorbents for Toluene Adsorption under Dry and Humid Conditions: Impacts of Pore Size and Surface Chemistry

Enhanced Vocs Adsorption over Zsm-5 Nanosheets with Different Thicknesses along the B-Axis