Abstract:Gold catalysts supported on titania (Au-TiO(2)) and alumina (Au-Al(2)O(3)) were prepared by deposition-precipitation with urea and then activated before characterisation and reaction in CO oxidation, either by calcination in air at 500 °C or reduction under H(2) at 300 °C. Gold nanoparticles with average size in the range 2-4 nm were obtained, with calcination leading to larger gold nanoparticles than reduction. For Au-TiO(2), high activity was observed in CO oxidation at room temperature, independent of the activation treatment. This high activity could not be correlated to the presence of sub-nanometer gold clusters as reported in the literature, since they could not be detected by atomic-resolution high-angle annular dark-field scanning-transmission electron microscopy (HAADF-STEM). In the case of Au-Al(2)O(3), the performance in CO oxidation was found to strongly depend on the water content in the reaction gas feed and on the activation conditions, with calcination resulting in a poorly active catalyst whereas reduction gave activity of the same order as Au-TiO(2). A comparative study of Au-TiO(2) and Au-Al(2)O(3) by electron microscopy did not reveal distinct differences in the shapes of the Au nanoparticles, which are mostly flattened through interaction with the substrate in both samples, with side profile shapes varying from rounded hemispherical to well faceted truncated cubo-octahedra. More faceting is found for the samples calcined at 500 °C than reduced at 300 °C. Various possible parameters affecting the catalytic properties of gold in CO oxidation are discussed in the context of the relevant literature.

Unveiling the gas-dependent sintering behavior of Au-TiO2 catalysts via environmental transmission electron microscopy

Direct in Situ TEM Visualization and Insight into the Facet‐Dependent Sintering Behaviors of Gold on TiO2

Simultaneous 2D Projection and 3D Topographic Imaging of Gas-Dependent Dynamics of Catalytic Nanoparticles

Revealing the Role of Surface Composition on the Particle Mobility and Coalescence of Carbon-Supported Pt Alloy Fuel Cell Catalysts by in Situ Heating (S)TEM

Atomic origin of CO-Interaction effect of PtPb@Pt catalyst revealed by in situ environmental transmission electron microscopy

Crystal-plane-dependent metal-support interaction in Au/TiO2

Quantitative Study of Au Catalytic Nanoparticles by Stem and Hrtem

In situ observation of catalyst nanoparticle sintering resistance on oxide supports via gas phase transmission electron microscopy

Dynamic Atom Clusters on AuCu Nanoparticle Surface During CO Oxidation.

Sintering behavior of carbon-supported Pt nanoparticles and the effect of surface overcoating

Environmental Transmission Electron Microscopy Study of the Origins of Anomalous Particle Size Distributions in Supported Metal Catalysts

In Situ Manipulation of the Active Au-TiO2 Interface with Atomic Precision During CO Oxidation.

In situ manipulation of the active Au-TiO 2 interface with atomic precision during CO oxidation

Reduced Sintering of Mass-Selected Au Clusters on SiO2by Alloying with Ti: an Aberration-Corrected STEM and Computational Study

HRTEM and STEM-HAADF characterisation of Au-TiO2 and Au-Al2O3 catalysts for a better understanding of the parameters influencing their properties in CO oxidation

Wet-Chemistry Strong Metal-Support Interactions in Titania-Supported Au Catalysts.

Investigating the impact of dynamic structural changes of Au/rutile catalysts on the catalytic activity of CO oxidation

Design and Preparation of Supported Au Catalyst with Enhanced Catalytic Activities by Rationally Positioning Au Nanoparticles on Anatase.

Surface Modification of Au/Tio2 Catalysts by Sio2 Via Atomic Layer Deposition

Revealing Correlation of Valence State with Nanoporous Structure in Cobalt Catalyst Nanoparticles by in Situ Environmental TEM

Exploring the key components of Au catalyst during CO oxidation using TG-MS and operando DRIFTS-MS