Abstract:The impact of a titania (TiO2) support film surface on the catalytic activity of gold nanoparticles (Au NP) was investigated. Using the reactive dc-magnetron sputtering technique, TiO2 films with an amorphous, anatase, and nitrogen-doped anatase crystal structure were produced for a subsequent role as a support material for Au NP. Raman spectra of these TiO2 films revealed that both vacuum and NH3 annealing treatments promoted amorphous to anatase phase transformation through the presence of a peak in the 513-519 cm-1 spectral regime. Furthermore, annealing under NH3 flux had an associated blue shift and broadening of the Raman active mode at 1430 cm-1, characteristic of an increase in the oxygen vacancies (VO). For a 3 to 15 s sputter deposition time, the Au NP over TiO2 support films were in the 6.7-17.1 nm size range. From X-ray photoelectron spectroscope (XPS) analysis, the absence of any shift in the Au 4f core level peak implied that there was no change in the electronic properties of Au NP. On the other hand, spontaneous hydroxyl (-OH) group adsorption to anatase TiO2 support was instantly detected, the magnitude of which was found to be enhanced upon increasing the Au NP loading. Nitrogen-doped anatase TiO2 supporting Au NP with ~21.8 nm exhibited a greater extent of molecular oxygen adsorption. The adsorption of both -OH and O2 species is believed to take place at the perimeter sites of the Au NP interfacing with the TiO2 film. XPS analyses and discussions about the tentative roles of O2 and -OH adsorbent species toward Au/TiO2 systems corroborate very well with interpretations of density functional theory simulations.

Quantitative Study of Au Catalytic Nanoparticles by Stem and Hrtem

HRTEM and STEM-HAADF characterisation of Au-TiO2 and Au-Al2O3 catalysts for a better understanding of the parameters influencing their properties in CO oxidation

Atomic-Scale Observation of Bimetallic Au-CuOx Nanoparticles and Their Interfaces for Activation of CO Molecules.

Structure-Sensitivity of Au Catalysis

Is Nanostructuring Sufficient To Get Catalytically Active Au?

Unique Structural Characteristics of Catalytic Palladium/Gold Nanoparticles on Graphene

X-ray Photoelectron Spectroscopy (XPS) Analysis of Ultrafine Au Nanoparticles Supported over Reactively Sputtered TiO2 Films

Electron Microscopy Investigations of Precious Metal Catalysts: Towards Controlled Synthesis of Ultra-Small Nanoparticles

A Comprehensive Study Of Catalytic, Morphological And Electronic Properties Of Ligand-Protected Gold Nanoclusters Using Xps, Stm, Xafs, And Tpd Techniques

Surface Structure Mediated Catalytic Activity Exhibition in Au Nanocrystals

A Comparative Dft Study of Adsorption and Catalytic Performance of Au Nanoparticles at Anatase and Brookite Tio2 Surfaces

Gold-Copper Nanoparticles: Nanostructural Evolution and Bifunctional Catalytic Sites

Reduced Sintering of Mass-Selected Au Clusters on SiO2by Alloying with Ti: an Aberration-Corrected STEM and Computational Study

Unveiling the gas-dependent sintering behavior of Au-TiO2 catalysts via environmental transmission electron microscopy

Atomically dispersed nano Au clusters stabilized by Zr on the TS-1 surface: Significant enhancement of catalytic oxidation ability using H<sub>2</sub> and O<sub>2</sub>

Morphology-dependent structures and catalytic performances of Au nanostructures on Cu2O nanocrystals synthesized by galvanic replacement reaction

Structural evolution of NiAu nanoparticles under ambient conditions directly revealed by atom-resolved imaging combined with DFT simulation.

A study on the morphology and catalytic activity of gold nanoparticles by the kinetic Monte Carlo simulation

Structure–activity Relationships in Supported Au Catalysts

Morphology-Dependent Evolutions of Sizes, Structures, and Catalytic Activity of Au Nanoparticles on Anatase TiO2 Nanocrystals

Crystal Structural Effect of AuCu Alloy Nanoparticles on Catalytic CO Oxidation.