High-Surface-Area Mesoporous Crystalline TiO2: Synthesis, Characterization, and Application As Support for Making Stable Au Catalysts
Yanfeng Dai,Shaodian Shen,Zhen Ma,Limeng Ma,Zuosong Sun,Jun Yu,Chuanyun Wan,Sheng Han,Dongseng Mao,Guanzhong Lu
DOI: https://doi.org/10.1166/jnn.2017.13988
2017-01-01
Journal of Nanoscience and Nanotechnology
Abstract:Au/TiO2 reported in the literature is highly active for CO oxidation, but it often suffers from high-temperature sintering and deactivation. Because the activation, application, and regeneration of Au/TiO2 often involve high temperature environments, it is necessary to enhance the thermal stability of the Au catalyst. In this work, we prepared mesoporous crystalline TiO2 (m-TiO2) with a high specific surface area (419 m(2)/g) via a soft/hard templating method. First, a m-TiO2/SiO2/C composite was prepared using fresh TiCl4 solution as a Ti source, TEOS as a Si source, resol as a carbon source, and F127 as a soft template, through an ethanolic evaporation-induced self-assembly (EISA) process. Then the carbon in the composite was removed by calcination in air, and the majority of the residual SiO2 was leached by a hot alkaline solution. The obtained m-TiO2 was used to load gold via deposition-precipitation. The resulting Au/m-TiO2 catalyst, containing a small portion of residual SiO2, was very active for CO oxidation, resistant toward thermal sintering at 600 degrees C, and stable during the stability test. The catalyst and related materials were characterized to demonstrate the mesostructure of the catalyst/support and the stabilization of gold nanoparticles upon thermal treatment.