Abstract:Four different thin film nanocomposite (TFN) membranes were prepared by adding different concentrations of porous Zr-MOFs (UiO-66 and UiO-66-NH2) to piperazine (PIP) aqueous solution (aqueous phase) or 1,3,5-Benzenetricarbonyl trichloride (TMC)-n-hexane solution (organic phase) by interfacial polymerization. The main purpose is to study the specific effects of different addition methods and addition amounts of nanoparticles on the structure and performance of the TFN membranes by interfacial polymerization. All four TFN membranes exhibited higher water permeability while maintaining high salt rejection compared to thin film composite (TFC) membrane. On the one hand, the TFN membranes behaves differently which are prepared by adding the same kind of nanoparticles to the aqueous phase or organic phase, respectively. The TFN membrane prepared by adding 0.2 w/v% UiO-66 to the organic phase had high water flux of 87.86 L·m-2·h-1, comparing 46.31 L·m-2·h-1 of membrane prepared by adding 0.3 w/v% UiO-66 in the aqueous phase. This is due to the fact that UiO-66 greatly slows the interfacial polymerization rate when UiO-66 is added to the organic phase, resulting in a thinner and more aperture polyamide thin film layer, reducing the water transmission resistance during filtration. Therefore, it is more economical by adding nanoparticles to organic phase than aqueous phase under the same filtering effect. On the other hand, different nanoparticles can also cause differences in performance and structure of the TFN membranes even in the same preparation manner. TFN membrane with UiO-66-NH2 in the aqueous phase has higher water permeance than the one with UiO-66 in the aqueous phase, owning to good hydrophilicity of amino group, which improves the water dispersibility of UiO-66-NH2, so that the TFN membrane is more uniform. In addition, UiO-66-NH2 slows down the process of interface polymerization, making the membrane more porous. The monomers in aqueous phase and the organic phase can be adsorbed in the pores of Zr-MOFs, which makes the interfacial polymerization occur both in the pores and on the surface of the pores. Thus, the compatibility between the polyamide and MOFs was enhanced and less defects was formed in the thin film layer, resulting in high salt rejection even the concentration of Zr-MOFs increased. This is the first time to explain that polyamide membrane has not obvious salt rejection attenuation with increasing porous material content using pore adsorption reaction monomer principle. Also, the Zr-MOFs based TFN membrane exhibited good heat resistance and anti-fouling property. This work shows that porous Zr-MOFs nanomaterials have significant advantages in the development of nanofiltration membranes with high water flux and rejection.

Interaction between MIL-101(Cr) and natural organic matter in an integrated MOF-UF system

Development of high-flux reverse osmosis membranes with MIL-101(Cr)/Fe3O4 interlayer

Impacts of Metal-Organic Frameworks on Structure and Performance of Polyamide Thin-Film Nanocomposite Membranes.

Construction of PPSU-MoS2/PA-MIL-101(Cr) Membrane with Highly Enhanced Permeance and Stability for Organic Solvent Nanofiltration

Continuation of a cleaning process: Application of MNBs-coagulation process to mitigate ultrafiltration membrane fouling

Fabrication of novel (Cr) based (MIL-101) incorporated mixed matrix forward osmosis membranes for environmental remediation

Microplastics and dye removal from textile wastewater using MIL-53 (Fe) metal-organic framework-based ultrafiltration membranes

Quantitative Assessment of Interfacial Interactions Governing Ultrafiltration Membrane Fouling by the Mixture of Silica Nanoparticles (SiO2 NPs) and Natural Organic Matter (NOM): Effects of Solution Chemistry

Characterization of Fouling in Immersed Polyvinylidene Fluoride Hollow Fibre Membrane Ultrafiltration by Particles and Natural Organic Matter

Zwitterionic metal-organic frameworks modified polyamide membranes with enhanced water flux and antifouling capacity

Probing the roles of Ca2+ and Mg2+ in humic acids-induced ultrafiltration membrane fouling using an integrated approach

Surface modification of nanofiltration membrane using polyoxometalates for improved separation and antifouling performance

Effects of UV/Fe(II)/sulfite pre-treatment on NOM-enhanced Ca2+ scaling during nanofiltration treatment: Fouling mitigation, mechanisms, and correlation analysis of membrane resistance

Effects of Coagulation on Submerged Ultrafiltration Membrane Fouling Caused by Particles and Natural Organic Matter (NOM)

MOF-808/Polyamide Thin-Film Nanocomposite Membranes for Efficient Nanofiltration

Fabrication of PVDF@MOF-303 membrane with Mortise-Tenon structure by the polyphenol analogue-assisted growth strategy for oil-water separation and heavy metal adsorption

Membrane Fouling Characteristics and Mitigation in a Coagulation-Assisted Microfiltration Process for Municipal Wastewater Pretreatment.

Zeolite Imidazolate Frameworks-8@SiO2-ZrO2 Crystal-Amorphous Hybrid Core-Shell Structure as a Building Block for Water Purification Membranes

[Enhancing PPCPs Removal and Membrane Fouling Control of Ultrafiltration Membrane by UiO-66@Fe3O4@UiO-66]

Porous Zr-based metal organic frameworks (Zr-MOFs) incorporated thin film nanocomposite membrane toward enhanced desalination performance.

Utilization of carboxyl group-grafted molybdenum disulfide for enhancing the performance of thin-film nanocomposite nanofiltration membranes