Abstract:This study examines the wettability behaviour of 304 stainless steel (304SS) and Ti-6Al-4V (Ti64) surfaces after sequential nanosecond (ns) and picosecond (ps) laser texturing; in particular, how the multi-scale surface structures created influence the lifecycle of surface hydrophobicity. The effect of different post-process treatments is also examined. Surfaces were analysed using Scanning Electron Microscopy (SEM), a white light interferometer optical profiler, and Energy Dispersive X-ray (EDX) spectroscopy. Wettability was assessed through sessile drop contact angle (CA) measurements, conducted at regular intervals over periods of up to 12 months, while EDX scans monitored elemental chemical changes. The results show that sequential (ns + ps) laser processing produced multi-scale surface texture with laser-induced periodic surface structures (LIPSS). Compared to the ns laser case, the (ns + ps) laser processed surfaces transitioned more rapidly to a hydrophobic state and maintained this property for much longer, especially when the single post-process treatment was ultrasonic cleaning. Some interesting features in CA development over these extended timescales are revealed. For 304SS, hydrophobicity was reached in 1-2 days, with the CA then remaining in the range of 120 to 140° for up to 180 days; whereas the ns laser-processed surfaces took longer to reach hydrophobicity and only maintained the condition for up to 30 days. Similar results were found for the case of Ti64. The findings show that such multi-scale structured metal surfaces can offer relatively stable hydrophobic properties, the lifetime of which can be extended significantly through the appropriate selection of laser process parameters and post-process treatment. The addition of LIPSS appears to help extend the longevity of the hydrophobic property. In seeking to identify other factors influencing wettability, from our EDX results, we observed a significant and steady rate of increase in the carbon content at the surface over the study period.

Anti-reflective and wetting properties of femtosecond pulsed laser textured Al alloy surfaces

Investigations in the fabrication of surface patterns for wettability modification on a Zr-based bulk metallic glass by nanosecond laser surface texturing

Influence of laser fluences and scan speeds on the morphologies and wetting properties of titanium alloy

Hydrophilic properties of the aluminum alloy induced by femtosecond laser structuring

Laser-induced selective wettability transition of 6061 aluminum alloy surfaces

Precision Fabrication of Micro-Textures Array for Surface Functionalization Using Picosecond Pulse Laser

The effect of surface texturing on the laser-induced wetting behavior of AlSi5 alloy on Ti6Al4V alloy

Parametric investigation of ultrashort pulsed laser surface texturing on aluminium alloy 7075 for hydrophobicity enhancement

Laser Textured Dimple-Patterns to Govern the Surface Wettability of Superhydrophobic Aluminum Plates

Fabrication of Anti-Reflective Surface with Superhydrophobicity/High Oleophobicity and Enhanced Mechanical Durability Via Nanosecond Laser Surface Texturing.

Analysis of anti-reflection mechanisms of the black aluminum alloy made by femtosecond laser processing

Investigation of open air and under water laser surface texturing on surface roughness and wettability of Al-Mg alloy

Influence of Instantaneous and Delayed Overlaps on Surface Topography and Wettability of a Femtosecond Laser Textured Surface

Experimental research on the fabrication and wettability of micro- and nano-scale surface textures produced on stainless steel using an ultrafast laser

Wetting and tribological properties of superhydrophobic aluminum surfaces with different water adhesion

Superhydrophobic Surfaces with Micro-/Nano-structures Prepared by Femtosecond Laser

Laser Texturing for Superwetting Titanium Alloy and Investigation of Its Erosion Resistance

Fabrication of super hydrophilic surface on alumina ceramic by ultrafast laser microprocessing

Wettability Behaviour of Metal Surfaces after Sequential Nanosecond and Picosecond Laser Texturing

An Experimental Study to Characterize a Surface Treated with a Novel Laser Surface Texturing Technique: Water Repellency and Reduced Ice Adhesion

Preparation of a superhydrophobic aluminium alloy surface by UV laser