Effect of heat treatment and extrusion processing on the microstructure and mechanical properties of spray formed 7055 alloy
Zhihong Jia,Zhiqiang Xie,Kaiyun Xiang,Lipeng Ding,Yaoyao Weng,Qing Liu
DOI: https://doi.org/10.1016/j.matchar.2021.111619
IF: 4.537
2022-01-01
Materials Characterization
Abstract:The effect of extrusion and heat treatment processes on the microstructure and mechanical properties of the spray formed 7055 alloy were systematically studied by three-dimensional X-ray microscope, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, atom probe tomography and tensile testing. It was found that the main second-phases in the as-deposited 7055 alloy include θ (Al2Cu) and Mg(Zn,Al,Cu)2 phases with similar structure to the ƞ (MgZn2) phase dissolved with Al and Cu. The Al2Cu particles embedded in Mg(Zn,Al,Cu)2 phase are widely distributed on the grain boundaries. Compared with the as-cast 7055 alloy, the S (Al2CuMg) phase and T (Al2Mg3Zn3) phases were not detected in the as-deposited alloy due to the change of solidification paths caused by rapid solidification. The microporosity caused by spray forming is always observed in the as-deposited alloy, these micro-pores can be effectively eliminated by the extrusion processing. Meanwhile, compared with extrusion directly after preheating at 420 °C/24 h, additional high temperature two-stage homogenization treatment before extrusion can reduce the adverse effect of S (Al2CuMg) phase and promote the precipitation of high density of Al3Zr dispersoids, which significantly increases the recrystallization resistance and improve the mechanical properties of the alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing