Failure Analysis on Rubber Universal Spherical Joints for Rail Vehicles

Chang Su,An-Xia Pan,Yi Gong,Zhen-Guo Yang

DOI: https://doi.org/10.1016/j.engfailanal.2021.105453

IF: 4

2021-01-01

Engineering Failure Analysis

Abstract:Considering the large quantity of passengers in a running rail vehicle, its safety must be paid special attention to, which relies on the reliability of every critical component. Spherical universal joint is widely used in the suspension device of the gearbox in the transmission of railway vehicles for its functions of damping and cushioning. Since it's commonly made of rubbers rather than the familiar metallic materials, its degradation behaviors and failure mechanisms have not been systematically investigated. In this study, multiple rubber spherical universal joints used in the urban rail transit train were found cracked and sticky during maintenance. Its design lifetime was 5 years, but this kind of failure occurred in <2 years, which posed a threat to the safe operation of the train. In order to identify the root causes of the failure, the physical, chemical, mechanical properties and the surface morphologies of the failed joints were characterized by a series of methods. The results showed that the corrosive solvents introduced during installation was the root cause of the failure, which was further aggravated by the oversizing and segregation of the filler particles in the rubber and the high crosslinking density of the rubber. Based on these failure causes, countermeasures were proposed to prevent the occurrence of similar failure again.