Preparation of Nano Cement Particles by Wet-Grinding and Its Effect on Hydration of Cementitious System
Maogao Li,Hongbo Tan,Xingyang He,Shouwei Jian,Zhengqi Zheng,Ying Su,Jin Yang,Yingbin Wang,Zhongtao Luo
DOI: https://doi.org/10.1016/j.conbuildmat.2021.125051
IF: 7.4
2021-01-01
Construction and Building Materials
Abstract:In this study, nano cement particles (Nano-C) were prepared via wet grinding cement. Nano-C was characterized by laser particle size distribution, X-ray diffraction (XRD), Thermogravimetric analysis (TGA), Scanning electron microscope (SEM), Transmission electron microscope (TEM) and Si-29 magic-angle spinning nuclear magnetic resonance (Si-29 MAS NMR). The particle size of Nano-C was D-50 = 53.1 nm. In order to disperse the nano particles, polycarboxylate superplasticizer was used in the process of grinding. The results show that 0.5%, 1.0%, 2.0%, and 4.0% Nano-C could increase the 12-h compressive strength by 49%, 109%, 194% and 197%, in comparison with the reference. The influence of Nano-C on the hydration, hydration products, microstructure was tested by means of hydration heat, chemical shrinkage, XRD, Thermogravimetric analysis (TGA), SEM, Si-29 MAS NMR, and Mercury injection porosimetry (MIP). The results revealed that Nano-C not only used as distinguished nucleus seed to enhance the PC system hydration but also exhibited high hydration activity to produce C-S-H gel to further raise the PC hydration up. These findings provided a novel way to prepare nano materials, which was expected to provide a way to improve the early strength of precast concrete.