Abstract:Nano-SiO2 is a brilliant candidate that endows cement-based materials excellent properties. However, its agglomeration in cement matrix is still an urgent problem. In order to address this issue, well-dispersed calcined stöber nano-SiO2 (CSNS) was prepared as modifier for Portland cement in this work. Monodisperse stöber nano-SiO2 (SNS) was firstly synthesized by using the traditional stöber method and then it was calcined to form CSNS. A series of properties including morphology and structure information of SNS and CSNS were obtained by using scanning electron microscope (SEM), particle size analyzer, X-ray diffraction (XRD), and fourier transform infrared spectroscopy (FT-IR). Their potential pozzolanic activity was also evaluated by using a simulated pore solution method and the possible reaction products were analyzed by using SEM and thermogravimetric (TG) analysis. Finally, their effects on early hydration properties of Portland cement were preliminarily investigated by using isothermal calorimetry, XRD, TG and compressive strength tests. The experimental results showed that both SNS and CSNS with high dispersity and uniform size within 100 nm were successfully prepared. However, both of them present low pozzolanic activity within 3 days. When 2 wt% SNS was added to cement, the occurrence of acceleration period was slightly delayed and the corresponding maximum heat flow was significantly reduced. Its addition also decreased both hydration degree of the cement paste and the compressive strength of the mortar at 1 day and 3 days. On the contrary, CSNS effectively overcame these negative effects of SNS on cement hydration, and further accelerated cement hydration. Compared with the Portland cement, the addition of 2 wt% CSNS significantly increased the cumulative heat released with 72 h, and cement hydration degree and compressive strength at each curing age. This is because the hydroxyl (-OH) group was removed after calcination of SNS, which made the well-dispersed CSNS better accelerate cement hydration by effective nucleation sites and filler effects. The findings of this work can provide a guidance for the application of well-dispersed nano-materials prepared based on stöber method to effectively modify the performance of cement-based materials.

Effects of highly dispersed nano-SiO 2 on the microstructure development of cement pastes

The acceleration effect of nano C-S-H-PCE on the microstructure formation and evolution at early age of cement paste

Synthesis of Nano-Sio2@ptpeg-vpa Copolymer and Its Effects on Early-Age Cement Hydration

Effect of Different Particle Sizes of Nano-Sio2 on the Properties and Microstructure of Cement Paste

Effect of nano‐SiO2 dispersion on the mechanical properties and frost resistance of modified cement paste

Influence of nano-silica agglomeration on microstructure and properties of the hardened cement-based materials

The effects of nano-C-S-H with different polymer stabilizers on early cement hydration

Effect of the specific surface area of nano-silica particle on the properties of cement paste

Comparative study on mechanisms for improving mechanical properties and microstructure of cement paste modified by different types of nanomaterials

Early hydration properties of Portland cement with lab-synthetic calcined stöber nano-SiO2 particles as modifier

Synergistic Effect and Mechanism of Nano-C-S-H Seed and Calcium Sulfoaluminate Cement on the Early Mechanical Properties of Portland Cement

Effect and mechanism of colloidal silica sol on properties and microstructure of the hardened cement-based materials as compared to nano-silica powder with agglomerates in micron-scale

Multi-scale Structure of In-Situ Polymerized Cementitious Composites with Improved Flowability, Strength, Deformability and Anti-Permeability

Enhancing cement hydration by core/shell PS@SiO 2 nanoparticles

Influence of Nano-SiO2 Content on Cement Paste and the Interfacial Transition Zone

Synergistic effects of CNTs/SiO2 composite fillers on mechanical properties of cement composites

Effects of Nano-CSH on the hydration process and mechanical property of cementitious materials

Effects of nano-C-S-H seed crystal on early-age hydration process of Portland cement

Effect of Nano-SiO2 on the Mechanical Properties, Microstructure, and Hydration Process of Cementitious Materials Incorporating Hydrophobic Admixture

Effect of the Nano-CaCO3 on Hydrated Properties and Interface of Cement Paste

INVESTIGATING THE EFFECT OF NANO SILICA ON THE MECHANICAL PROPERTIES OF HARDENED CEMENT PASTE