Middle-low Temperature Sintering and Piezoelectric Properties of CuO and Bi2O3 Doped PMS-PZT Based Ceramics for Ultrasonic Motors

Shun Li,Jian Fu,Ruzhong Zuo

DOI: https://doi.org/10.1016/j.ceramint.2021.04.018

IF: 5.532

2021-01-01

Ceramics International

Abstract:A ternary solid-solution piezoelectric ceramic of rare-earth oxides modified 0.03 Pb(Mn1/3Sb2/3)O3-0.97 Pb (Zr0.505Ti0.495)O3 + x wt.% CuO + y wt.% Bi2O3 (PMS-PZT + x wt.% CuO + y wt. % Bi2O3) (x, y = 0-0.2) was successfully prepared via a transient-liquid-phase sintering. Both Cu2+ and Bi3+ were believed to replace the Asite Pb ions and to evidently induce the lattice shrinkage and the distortion decrease. However, the addition of only a small amount of CuO was found to effectively reduce the sintering temperature, sustain good piezoelectric properties and predominant transgranular fracture modes, but obviously increase the average grain size and high-field dielectric loss. Further experimental results indicate that the grain growth of the ceramics was inhibited effectively and the high-field dielectric loss was reduced through CuO and Bi2O3 co-doping. The 0.05 wt% CuO and 0.15 wt% Bi2O3 co-doped PMS-PZT ceramics sintered at 1050 degrees C exhibit excellent dielectric and piezoelectric properties of d33 = 410 pC/N, kp = 0.62, Qm = 1478, epsilon r = 1550, tan delta = 0.8% (400 V/mm) and Tc = 330 degrees C. The experimental results can provide a solid fundament for multilayer piezoelectric actuating devices.