Abstract:Black TiO2−x is an attractive material due to its adjustable band structure, useful in different applications, and has been heavily investigated and developed. The current reduction of TiO2 involves a process from surface to center: thus, the issue of either insufficient or excessive reduction seems inevitable. To the best of our knowledge, it is rarely reported that a homogeneous defect distribution can be facilely achieved inside black TiO2−x. In this study, a bulk-reduced rutile TiO2−x was obtained via a circuitous two-step approach, with an intermediate Magneli phase (TinO2n−1). With the decomposition of a solid atmosphere creator (e.g. KClO4 grains) at a high temperature, the missing oxygen ions in Ti4O7 could be replenished quantitatively. The TEM and SAED results reveal that the oxidation process is not just a surface reaction, but it involves reverse displacement or structural rearrangement inside the crystal. In particular, the periodic variation of crystallographic sheer planes was the direct evidence of the above bulk reaction, i.e. unified long period for Ti4O7 and varied long period for critical ratio sample. The as-prepared samples showed different band gaps and colors, based on their oxygen content. KClO4, with a critical mixing ratio of around 17.5 mol%, could almost oxidize Ti4O7 to black rutile TiO2−x. Furthermore, the sample formed at the critical ratio showed a considerable photo-thermal response speed of 1.7 °C s−1 and an equilibrium temperature of up to 70 °C under irradiation with light above 400 nm, which can be an evidence for the enhancement of non-intrinsic absorption. In short, this study provides a new route for the controllable preparation of black TiO2−x, and a possibility for further development of other solid atmosphere creators.

A Unique Black TiO2 Created from CO-induced Oxidation of Defect-Rich TiO2

A Reverse Slipping Strategy for Bulk-Reduced TiO2−x Preparation from Magnéli Phase Ti4O7

A Safe and Efficient Approach to Fabricate Black Carbon-Doped Rutile Titania by Substitution of Oxygen at Carbon Sites in Titanium Carbide Film

A Facile Approach to Prepare Black TiO2 with Oxygen Vacancy for Enhancing Photocatalytic Activity

Self-assembly of a Highly Stable and Active Co3O4/H-TiO2 Bulk Heterojunction with High-Energy Interfacial Structures for Low Temperature CO Catalytic Oxidation

Extension of the Optical Absorption of Tio2 Nanopaticles to Visible Light Region by Doping with Cobalt

A Ti-OH bond breaking route for creating oxygen vacancy in titania towards efficient CO2 photoreduction

Black brookite rich in oxygen vacancies as an active photocatalyst for CO2 conversion: experiments and first-principles calculations

S-scheme heterojunction of black TiO2 and covalent-organic framework for enhanced photocatalytic hydrogen evolution

Controllable preparation of black titanium dioxide and its wave-absorbing properties

In Situ Tuning of Defects and Phase Transition in Titanium Dioxide by Lithiothermic Reduction

Black TiO2 synthesized via magnesiothermic reduction for enhanced photocatalytic activity

Fabrication of Black In2O3 with Dense Oxygen Vacancy through Dual Functional Carbon Doping for Enhancing Photothermal CO2 Hydrogenation

Enhanced Photocatalytic Reduction of Carbon Dioxide into Carbon Monoxide by Electric Field Generation and Defect Engineering in TiO2

Black TiO2 for solar hydrogen conversion

Effective Formation of Oxygen Vacancies in Black Tio2 Nanostructures with Efficient Solar-Driven Water Splitting

The Self‐sacrificial Templated Synthesis of Fe/N Co‐doping TiO2 for Enhanced CO2 Photocatalytic Reduction

The Origin Of Enhanced Photocatalytic Activities Of Hydrogenated Tio2 Nanoparticles

Colloidal TiO2 Nanocrystals with Engineered Defectivity and Optical Properties

Modification of TiO2 Nanoparticles with Organodiboron Molecules Inducing Stable Surface Ti3+ Complex

Synergy of oxygen vacancy and electron donor in one-dimensional black TiO 2 /phosphotungstic acid with Z-scheme heterojunctions for enhanced photocatalytic CO 2 reduction