Effect of co-precipitation plus spray-drying of nano-CaF₂ on mechanical and fluoride properties of nanocomposite

Quan Dai,Michael D. Weir,Jianping Ruan,Jin Liu,Jianghong Gao,Christopher D. Lynch,Thomas W. Oates,Yuncong Li,Xiaofeng Chang,Hockin H. K. Xu

DOI: https://doi.org/10.1016/j.dental.2021.03.020

2021-01-01

Abstract:Objective. Fluoride (F)-releasing restoratives typically are either weak mechanically or release only low levels of F ions. The objectives of this study were to: (1) develop a novel photo-cured nanocomposite with strong mechanical properties and high levels of sustained F ion release via a two-step "co-precipitation + spray-drying" technique to synthesize CaF2 nanoparticles nCaF(2)); and (2) investigate the effect of spray-drying treatment after co-precipitation of CaF2 on mechanical properties and F ion release of composite. Methods. Two types of CaF2 particles were synthesized: A co-precipitation method yielded CaF(2)cp; "co-precipitation + spray-drying" yielded nCaF(2)cpsd. Composites were fabricated with fillers of: (1) 0% CaF2+ 70% glass; (2) 10% CaF(2)cp + 60% glass; (3) 15% CaF(2)cp + 55% glass; (4) 20% CaF(2)cp + 50% glass; (5) 10% nCaF(2)cpsd + 60% glass; (6) 15% nCaF(2)cpsd + 55% glass; and (7) 20% nCaF(2)cpsd + 50% glass. A commercial F-releasing nanocomposite served as control. Results. The nCaF(2)cpsd had much smaller particle size (median = 32 nm) and narrower distribution (22-57 nm) than CaF(2)cp (median = 5.25 mu m, 162 nm-67 mu m). The composite containing nCaF(2)cpsd had greater flowability, flexural strength, elastic modulus and hardness than CaF(2)cp composite and commercial control composite. At 84-day immersion in water, the nanocomposites containing 20% nCaF(2)cpsd had 65 times higher cumulative F release, and 77 times greater long-term F-release rate, than commercial control. Conclusions. A novel two-step "co-precipitation + spray-drying" technique of synthesizing nCaF(2) was developed. The photo-cured nanocomposite containing 20% nCaF(2)cpsd possessed strong mechanical properties and excellent long-term F-release ability, and hence is promising for dental restoration applications to inhibit secondary caries. (C) 2021 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.