Analysis of corrosion of A n thermal storage Na₂HPO?12H₂O by molecular dynamics

Rao Dou,Maosheng Zheng

DOI: https://doi.org/10.1680/jnaen.19.00015

2020-01-01

Nanomaterials and Energy

Abstract:Molecular dynamics is employed to analyze the corrosion of aluminum in molten sodium hydrogen phosphate dodecahydrate (Na2HPO4 center dot 12H(2)O) hydrate salt phase-change material and the inhibition effect of 3.25% sodium metasilicate nonahydrate (Na2SiO3 center dot 9H(2)O) and 1% sodium chromate tetrahydrate (Na2CrO4 center dot 4H(2)O) additions. The corrosion of aluminum in a dilute solution of 3% sodium hydrogen phosphate is calculated comparatively. The results show that the diffusion coefficients of hydrogen phosphate (HPO42-) and water (H2O) in the pure molten sodium hydrogen phosphate dodecahydrate are 4.65 x 10(-9) and 1.80 x 10(-8) m(2)/s, respectively. When 3.25% sodium metasilicate nonahydrate and 1% sodium chromate tetrahydrate are added to the molten sodium hydrogen phosphate dodecahydrate, the coverage degrees of metasilicate (SiO32-) and chromate (CrO42-) are 78 and 84% in molten sodium hydrogen phosphate dodecahydrate solution, the diffusion coefficients of hydrogen phosphate reduce to 1.34 x 10(-9 )and 1.01 x 10(-9) m(2)/s, and the corresponding diffusion coefficients of water are 4.35 x 10(-9) and 1.05 x 10(-8 )m(2)/s, respectively. This indicates the obvious inhibition effect of the additions of sodium metasilicate nonahydrate and sodium chromate tetrahydrate. Comparatively, the reduction of diffusion coefficients of hydrogen phosphate and water in the similar cases is not too much.