Integral-type low-temperature SCR denitration catalyst and preparation method thereof

Zhang Yaping,Zhu Yiwen,Xiao Rui,Huang Tianjiao,Xu Haitao,Shen Kai

2017-01-01

Abstract:The invention discloses an integral-type low-temperature SCR denitration catalyst and a preparation method thereof. The integral-type low-temperature SCR denitration catalyst comprises 24%-48% of titanium dioxide, 12%-16% of manganic oxide, 1%-10% of holmium oxide, 5%-9% of iron sesquioxide, 3%-8% of glass fibers, 2%-5% of cellulose glycolate, 3%-6% of glycerinum, 0.7%-2% of activated carbon powder and 21%-26% of water. The preparation method includes the steps that the titanium dioxide, the manganic oxide, the holmium oxide, the iron sesquioxide, the glass fibers, the cellulose glycolate and the activated carbon powder are mixed, and then the glycerinum and the water are added to prepare paste; and the paste is subjected to ageing, compression molding forming, drying and calcination, and accordingly the integral-type low-temperature SCR denitration catalyst can be obtained. The integral-type low-temperature SCR denitration catalyst and the preparation method thereof have the advantages that the denitration catalyst has good low-temperature activity, the NOx conversion rate can reach about 95% under the temperature condition of 120 DEG C, the denitration efficiency is high and the mechanical property is also high; and meanwhile, the preparation method is high in operability, an ideal catalyst forming effect can be achieved, the process is simple and the rate of finished products is high.