Quantitative Analysis of Alloying Elements in Titanium Alloy by Laser-Induced Breakdown Spectroscopy(LIBS)
Lei Tianyu,Zhang Yong,Liu Ying,Zhang Zhiming
DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16032204
2018-01-01
Abstract:Titanium alloy samples were induced by solid state Nd:YAG laser, of which the output wavelength was 1064 nm, echelle spectrograph was used to disperse compound light , intensified charge-coupled device ( ICCD) was used to detect optical signal , and the contents of alloying elements in titanium alloy were determined by laser-induced breakdown spectroscopy ( LIBS) .For a better analysis capability of LIBS, the parameters of delay time were optimized and the best delay time was determined as 2μs finally.Under the opti-mized conditions , the calibration curves were made by a series of certified TC 11 titanium alloy samples for five elements , Al, Mo, Zr, Fe, and Si, and the contents of alloying elements in TC 11 sample were quantified .The results indicated that the detection limit of LIBS were 8.98 ×10 -4(Al), 8.43 ×10 -4(Mo), 4.99 ×10 -4(Zr), 1.73 ×10 -4(Fe) and 4.03 ×10 -4(Si), respectively.The contents (mass fraction) of Al, Mo, Zr, Fe and Si were 6.84%, 3.24%, 1.55%, 0.11%, and 0.26%.T-test method was used to compare the results of LIBS with national standard method GB/T 4698.2-4698.3 and to test the accuracy of the method.The t values of Al, Mo, Zr, Fe and Si were 1.37, 1.63, 0.82, 0.61, 1.83 respectively, which were all less than the critical value of 95%confidence probability (t0.05,6 =2.45).The results showed that LIBS was a fast and effective for quantitative analysis of titanium alloy samples.