Abstract:One of the ways to obtain high-quality products and meet ever-increasing requirements on properties of steel is microalloying it with rare earth elements such as cerium. Cerium can significantly affect mechanical properties of steel even at low concentrations. To reduce the cost of steel, it is rational to add cerium into steel not with ferroalloys but by direct reduction from oxide systems. In order to study this process, thermodynamic modeling of the reduction of cerium from slags of the CaO–SiO2–Ce2O3 system, containing 15% Al2O3 and 8% MgO, with aluminum and calcium carbide at temperatures of 1 550 and 1 650°C is carried out. The simulation is performed using the HSC 6.12 Chemistry software package (Outokumpu) based on Gibbs energy minimization and using the simplex planning lattice method. The results of thermodynamic modeling are presented in the form of composition-property (equilibrium cerium content in the metal) diagrams for temperatures of 1 550 and 1 650°С. When using metallic aluminum as a reducing agent, increasing the basicity of the slag (CaO/SiO2) from 2 to 5 at a temperature of 1 550°C leads to an increase in the equilibrium cerium content in the metal from 2 to 20 ppm in the concentration range of 0–15٪ Ce2O3, i.e. an increase in the basicity of the slag is beneficial for the development of the cerium reduction process. An metal temperature increase also has a positive effect on the process of reduction of cerium with aluminum. With an increase in temperature to 1 650°С, the equilibrium content of cerium in the metal increases from 4 ppm to 30 ppm in the concentration range of 0–15٪ Ce2O3. The use of calcium carbide as a reducing agent leads to an increase in the concentration of cerium in the metal to 30 and 40 ppm at temperatures of 1 550 and 1 650°C, respectively, at a basicity of 5. The decisive role of slag basicity, cerium oxide concentration and temperature in the development of the process of cerium reduction with aluminum and calcium carbide is confirmed.

Reaction Behaviour Between Cerium Ferroalloy and Molten Steel During Rare Earth Treatment in the Ultra-low Carbon Al-killed Steel

Influence of cerium treatment on inclusion modification and as-cast microstructure of high-strength low-alloy steel

Effect of CeAlO3 refractories on the cleanliness of rare earth treated steel

Effect of cerium on the primary carbides and inclusions in electroslag remelted M35 high speed steel

Effect of Cerium Addition on Microstructure and Mechanical Properties of As-Cast High Grade Knives Steel

Effect of Cerium on the Cleanliness and Properties of an Al‐Killed Low‐Sulfur Steel

Effect of Cerium Content on Inclusions in an Ultra-Low-Carbon Aluminum-Killed Steel

Analysis of the micro-alloying effect of cerium additions to the Al-Li alloy 2090

Effect of rare earth La–Ce on solidification structure of 3.2%Si-0.9%Al non-oriented silicon steel

Interaction Behaviors of Ce‐Treated Al‐Killed Steel Grades with Different Refractories

Experimental Study on Thermodynamics of CaO–SiO2–Ce2O3–5wt.% Al2O3 System at 1773 K

Thermodynamic Analysis of the Oxidation Behavior of Cerium in High‐Speed Steel during Electroslag Remelting

Steel–refractory reactions in lanthanum-, cerium-, and yttrium-added steels

Study of the process of cerium restoration by aluminum and calcium carbide from cerium-containing slag

Study on Influence of Rare Earth Ce on Micro and Macro Properties of U75V Steel

Influence of Refractory-Steel Interfacial Reaction on the Formation Behavior of Inclusions in Ce-containing Stainless Steel

Effect of Cerium on Inclusion Modification in a Secondary-Hardening Steel

Effect of cerium addition on non-metallic inclusions in a high-carbon chromium bearing steel

Study on mechanism of refining and modifying in Al-Si-Mg casting alloys with adding rare earth cerium

Cerium refinement of grains and primary carbides during solidification of Cr4Mo4V bearing steel