Synthesis and Properties of Magnetic Ferric Oxide/SO2-4 Biomass-based Solid Acid Catalyst

Xueqin Li,Yao Chen,Xiangyu Li,Junyou Shi,Tingzhou Lei,Xixin Duan,Gaofeng Chen

DOI: https://doi.org/10.11713/j.issn.1009-4822.2017.02.029

2017-01-01

Abstract:Two kinds of magnetic ferric oxide particles were prepared through glycol and sodium sulfite methods.Magnetic ferric oxide/SO2-4 biomass-base solid acid catalysts were synthesized via loading the magnetic ferric oxide particles into the sulfuric acid treated biomass-base precursor.The catalyst activities,such as surface acid amount,magnetic response properties and reducing sugar yield (DNS method) from catalytic hydrolyzed micro-crystalline cellulose were evaluated.The structures of the catalyst were characterized by XRD,FT-IR,Raman,SEM and VSM.The results showed that the catalyst activity and structure are quite different from different synthesis methods.Compared with the catalyst prepared from PEG method,the acid density for 1.13mmol/g,reducing sugar yield for 30%,carbon content of the catalyst by the sodium sulfite method are much higher,and the cycle of preparation process is moderate(2970min).At the same time,the magnetic Ferric Oxide load particles amount is also higher,the specific surface area is larger,channel structure is richer.VSM analysis showed that the catalyst prepared by polyethylene glycol method was ferromagnetic material,and the catalyst prepared by sodium sulfite was ferrous magnetic materials.