Study on performances and preparations of oxide layer with corrosion and wear resistance on new β-type Zr-20 Nb-7 Ti alloy

Jian-feng ZHANG,Hong-qun TANG,Xia-xia GAN,Yong-zhong ZHAN
DOI: https://doi.org/10.13624/j.cnki.issn.1001-7445.2017.1823
2017-01-01
Abstract:In clinical, the wear resistance of Ti and its alloys is poor and the elastic modulus of them don't match the bones and teeth of human body. In order to research and develop materials with low elasticity modulus, good wear resistance and corrosion resistance for biomedical applications, theβ-type Zr-20Nb-7Ti alloys were oxidized at 550℃ for 5 min, 30 min, 45 min, 60 min, respectively. The SEM images show that smooth compact oxidized layer with 8. 1 μm thickness can be in-situ formed on the surface of the Zr-20Nb-7Ti by thermal oxidation at 500℃ for 30 min. The hardness of the Zr-20Nb-7Ti alloy increase from 267 HV to 934 HV after thermal oxidation. The electrochemical corrosion test in artificial saliva showed that the corrosion potential of Zr-20 Nb-7 Ti alloy increased from -0. 48939 V to -0. 27121 V, corrosion current of Zr-20Nb-7Ti alloy increased from 0. 73104 μA/cm2 to 0. 054152 μA/cm2 and corrosion rate of Zr-20Nb-7Ti alloy increased from 0. 81318 μm/a to 0. 059872 μm/a after thermal oxidation. The wear test performed on pin-on-disk wear tester in artificial saliva indicated that the COF of the Zr-20 Nb-7 Ti alloy decreased from 0. 60 to 0. 23 and wear loss of the Zr-20 Nb-7 Ti decreased from 26. 39 mg to 0. 31 mg after thermal oxidation . The results show that oxidized layer on Zr-20 Nb-7 Ti alloy made through thermal oxidation at 500 ℃ for 30 min improves the wear resistance and corrosion resistance of the alloy, and the oxidized Zr-20Nb-7Ti alloy meets the requirements of the biomedical materials.
What problem does this paper attempt to address?