Hot deformation behavior of BFe30-1-1 alloy and its hot processing map

Xiao-jun WANG,Hao-dong LUO,Cheng-peng MIAO

DOI: https://doi.org/10.3969/j.issn.1673-5196.2017.06.002

2017-01-01

Abstract:Hot deformation behavior of BFe30-1-1 alloy was investigated in temperature range from 750 ℃ to 1 000 ℃ and in strain rate range from 0.1 s-1 to 10 s-1 by means of high-temperature compression test on Gleeble-1500D thermal simulator.The true stress vs true strain curve of BFe30-1-1 alloy at high temperature was acquired thereby and the variation regularity of its rheologic stress was analyzed,also.The hot deformation equation of BFe30-1-1 alloy was established,its hot processing maps were drawn on the basis of dynamic materials model,and the maps were analyzed based on the microstructure of the compressed alloy.It was found thereby that the deformation conditions would have significant influence on the hot processing maps;the energy dissipation rate would be greater under the condition of lower strain rate and higher temperature.On the basis of hot processing maps with strain rate of 0.2,0.4,0.6,and 0.8 respectively,the structural characteristics of dynamic recrystallization and the microstructure of rheologic stability-collapse of the alloy were analyzed and it was found finally that the optimal hot processing temperature range would be from 830 ℃ to 950 ℃ and strain rate range would be from 0.01 s-1 to 0.05 s-1 for BFe3-1-1 alloy.