Abstract:The 2195 Al-Cu-Li alloy is widely utilized for the fabrication of key aerospace vehicle components; hence, an in-depth understanding of its hot deformation behavior is essential for consistently achieving high-performance products. In this study, isothermal compression tests were performed on 2195 Al-Cu-Li alloy ingots in the temperature and strain rate ranges of 250–500 °C and 10 −3 -1 s −1 , respectively. A processing map was established to predict the workability under different conditions. The corresponding microstructures were examined to reveal their hot deformation mechanism. Results demonstrated that the processing map was divided into four distinct domains. The unstable zone was located in the 250–375 °C/10 −1.5 -1 s −1 and 250–275 °C/10 −2.5 –10 −1.5 s −1 , temperature/strain rate regimes, in which deformation bands and flow localization were observed. The deformation bands blocked dislocations and compromised the dynamic recrystallization (DRX) behavior, hence damaging the microstructure. Further, large coarse T 1 phases precipitated in the 325–410 °C/10 −2.5 –10 −3 s −1 regime, which led to the formation of heterogeneities in the microstructure, corresponding to a minimum workability in the processing map. The optimal hot-working domain for the 2195 alloy was determined to be 460–500 °C/10 −3 –10 −2 s −1 , and the dominating hot deformation mechanisms were DRX and dynamic recovery (DRV). Specifically, continuous and discontinuous DRX behaviors dominated in the 300–400 °C/10 −3 s −1 and 450–500 °C/10 −3 s −1 regimes, respectively. DRX gradually weakened as the strain rate increased at 500 °C. Further, the weakening of DRX was only minimally affected by temperature at 400–500 °C during high-speed deformation (1 s −1 ). The results reported herein can provide valuable insights into the hot working of Al-Cu–Li alloys.

Hot Deformation Behavior and Microstructural Evolution of a New Type of 7xxx Al Alloy

Hot Deformation Behavior and Microstructure Evolution of Al-7.92 Zn-1.64 Mg-2.00 Cu Alloy

Hot Deformation Behavior of Homogenized Al-7.8Zn-1.65Mg-2.0Cu (wt.%) Alloy

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Hot Workability and Microstructure Evolution of Homogenized 2050 Al-Cu-Li Alloy during Hot Deformation

Hot Deformation Characteristics and Processing Parameter Optimization of Al–6.32Zn–2.10Mg Alloy Using Constitutive Equation and Processing Map

Hot deformation behavior of high Zn-containing 7A65 Al alloy

Characterization of Hot Deformation Behavior and Processing Maps of Homogenized Al-Mg-Si-Sc-Zr Alloys

Constitutive behavior and novel characterization of hot deformation of Al-Zn-Mg-Cu aluminum alloy for lightweight traffic

Hot deformation behavior and microstructural evolution of the Al-Cu-Li alloy: A study with processing map

Hot Deformation Behavior and Processing Map of Al-Zn-Mg-Cu-Zr Alloy

Hot Deformation Behavior and Microstructure Evolution of a Novel High-Zn Containing Al-Zn-Mg-Cu-Zr Alloy

Hot Deformation and Dynamic Recrystallization of 7075 Al Alloy in the Extruded State

Hot deformation behavior and process parameters optimization of GH4738 nickel-based superalloy

Hot Deformation Behavior and Dynamic Softening Mechanism in 7B50 Aluminum Alloy

Hot Deformation Behavior and Processing Maps of an As-Cast Al-5Mg-3Zn-1Cu (wt%) Alloy

Hot Deformation Behaviors of the Mg-3Sn-2Al-1Zn Alloy: Investigation on its Constitutive Equation, Processing Map, and Microstructure

Hot deformation characteristics and processing parameter optimization of 2219 Al alloy using constitutive equation and processing map

Hot deformation characteristics and processing maps of AA7075-H18 alloy sheet under hot forming process conditions

Hot Processing Map and Dynamic Precipitation Behavior of 1460 Al–Li Alloy During Hot Deformation

Hot compression behaviors and microstructural evolution of Be-38wt.%6061Al