Effect of matrix materials hardness and roughness on adhesion of TiAlCN coatings

Yong ZHANG,Xin-an DANG,Li-jun YANG,Ze-hui ZHANG,Lin LI

DOI: https://doi.org/10.3969/j.issn.1000-5811.2014.01.016

2014-01-01

Abstract:The composite TiAlCN coatings were deposited by vacuum arc ion plating on GCr15 rings with different matrix materials hardness and roughness at 175 ℃ .The analysis results of SEM ,AFM ,EPMA ,XRD ,adhesion tester indicated :as the substrate surface roughness ,the preparation of the coating surface would be smooth .Film adhesion decreased with the increased of surface roughness .When the roughness was 0 .01 μm ,the film adhesion was up to the maximum of 42 .8 N .The higher the hardness of matrix ,the greater the adhe-sion of film/substrate was obtained .As the substrate hardness was 835 HV0 .01 ,the maxi-mum adhesion was 31 .2 N .The crystal structure of fcc-structure of TiN was found in the film .The diffraction pattern without AlN phase ,it was because of TiN phase was better than that of AlN phase formation .