Abstract:Abstract Mesoporous silica (MS) was prepared through a simple self‐assembly procedure under alkaline condition with tetraethyl orthosilicate (TEOS) as SiO 2 precursor and cetyltrimethyl ammonium bromide (CTAB) as the template. A series of shape‐stabilized composite phase change materials (ss‐CPCMs), using polyethylene glycol 6000 (PEG6000) as the PCM and MS as the matrix with different mass percentage of PEG6000 loadings, was prepared through a vacuum impregnation method. N 2 adsorption‐desorption analyzer measurement showed the specific surface area and average pore size of the as‐prepared porous silica were determined to be 760 m 2 /g and about 3 nm, respectively. Differential scanning calorimetry (DSC) measurements indicated that the melting peak temperatures and latent heats of melting of the composites are varied from 52.3°C to 62.6°C and 32.9 to 186.4 J/g (PEG6000 mass fractions: 0%‐80%), which was proportional to PEG6000 content. Fourier‐transform infrared (FT‐IR) spectroscopy results implied that only the physical interaction existed between the PEG6000 and SiO 2 matrix. The shape‐stability measurements suggested the composite with the 70% mass loading of PEG6000 can still maintained the original shape and no leakage were observed above the much higher melting temperature of PEG6000 (105°C). Thermal cycling test showed that the ss‐CPCM had good thermal reliability and chemical stability although it was experienced 500 melting and cooling cycles. Moreover, the thermal decomposition temperature of the composites (393.2°C) was much larger than the melting temperature of pure PEG6000 (62.6°C), which indicated that composite presented excellent thermal stabilities and was suitable for thermal energy storage applications.

Preparation,characterization and thermal performanceof the PEG/CF composite phase change materials

Preparation and Properties of Paraffin /LDPE /OMMT /graphite Phase Change Composite for Thermal Energy Storage

Preparation and Characterization of Polyethylene Glycol/active Carbon Composites As Shape-Stabilized Phase Change Materials

Preparation and characterization of polyethylene glycol‐based form‐stable phase change materials supported by poly (vinyl formal) foams

The Shape-Stabilized Phase Change Materials Composed Of Polyethylene Glycol And Various Mesoporous Matrices (Ac, Sba-15 And Mcm-41)

Polyethylene Glycol–Calcium Chloride Phase Change Materials with High Thermal Conductivity and Excellent Shape Stability by Introducing Three-Dimensional Carbon/Carbon Fiber Felt

Preparation and Characterization of Fatty Acid Ternary Eutectic Mixture/Nano-Sio 2 Composite Phase Change Material for Building Applications

Preparation and characterization of eicosane-paraffin/expanded graphite/polyurethane as form-stable composite phase change materials with wide phase change temperature range

Shape-stabilized Phase Change Materials Based on Polyethylene Glycol/porous Carbon Composite: the Influence of the Pore Structure of the Carbon Materials

Using mesoporous carbon to pack polyethylene glycol as a shape-stabilized phase change material with excellent energy storage capacity and thermal conductivity

Investigation on interfacial interaction and thermal properties of flame retarded wood-plastic form-stable phase change material

Thermal conductivity enhancement of polyethylene glycol/NF composite as stabilized phase change materials for thermal energy storage

Using surface-modified UiO-66 with hierarchical pores to pack polyethylene glycol for phase change thermal energy storage: Experiment and molecular dynamics simulations

Preparation and thermal performance of polyurethane/PEG as novel form-stable phase change materials for thermal energy storage

Recent Progress in PEG-Based Composite Phase Change Materials

Morphology, thermal and mechanical properties of electrospun polyvinylidene/polyethylene glycol composite nanofibers as form-stabilized phase change materials

Study on the Preparation and Properties of PEG Phase Change Materials Fixed by Semi-IPN

Preparation and Thermal Properties of Propyl Palmitate-Based Phase Change Composites with Enhanced Thermal Conductivity for Thermal Energy Storage

Mica-stabilized polyethylene glycol composite phase change materials for thermal energy storage

Preparation and thermal properties of shape‐stabilized polyethylene glycol/mesoporous silica composite phase change materials for thermal energy storage

Preparation and Characterization of Bio-Based PLA/PEG/g-C3N4 Low-Temperature Composite Phase Change Energy Storage Materials