Abstract:Phosphogypsum (PG) is a kind of industrial solid waste with high impurity content and low utilization rate. In this study, α-hemihydrate gypsum (α-HH) was synthesized from PG in H3PO4–H2O solution (wet-process phosphoric acid solution and phosphoric acid solution) under atmospheric pressure. The crystal morphology of α-HH was controlled by adding F and Al compound regulators, and the mechanical properties of α-HH were improved. The difference of α-HH synthesized by PG with different qualities was analyzed, and the mechanism of α-HH morphology was studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy-dispersive spectroscopy (EDS). Results showed that in the wet-process phosphoric acid solution, α-HH synthesized from white PG (by H3PO4–H2SO4 two-step method) had better whiteness, purity, and mechanical properties compared with that from industrial PG, and the performance indexes of the α-HH products met the requirements of α50 grade in JC/T 2038–2010 α-high-strength gypsum in China and have a good commercial application prospect. Moreover, in the phosphoric acid solution, the average diameter of the α-HH crystal increased from 8.1 µm to 54.8 µm, the average aspect (L/D) ratio decreased from 32.65 to 0.52, and the induction period and growth period of the α-HH crystal were prolonged with the increase in regulator dosage. F− and Al3+ ions were preferred to adsorb on the crystal faces. The growth of the crystal parallel to c-axis (200), (020), and (400) was inhibited, and the morphology of the α-HH crystal changed from whisker to short column. When the dosage of the regulator was 1.1 %, the 2 h bending strength of the α-HH product was 6.56 MPa, and the drying compressive strength was 52.4 MPa. This study provides a new technique and method for the synthesis of high-strength α-HH products from PG.

Study on Process Conditions for Preparation of α-high Strength Gypsum by the Glycerol Water Method under Atmospheric Pressure

Study on Preparation of High-Strength Gypsum by FGD Gypsum

Preparation of α-hemihydrate gypsum from phosphogypsum in glycerol and Na2SO4 mixed solutions under atmospheric pressure

Synthesis of α-hemihydrate gypsum from cleaner phosphogypsum

Preparation of Medium–Low Strength Hemihydrate Gypsum from Phosphogypsum and Grey Correlation Evaluation of Autoclaving Energy Consumption

Preparation of α-hemihydrate gypsum whiskers from phosphogypsum using atmospheric pressure nitrate solution

Facile Preparation of High-Strength Α-Caso 4 ·0.5H 2 O Regulated by Maleic Acid from Phosphogypsum: Experimental and Molecular Dynamics Simulation Studies

Facile preparation of high-strength α-CaSO4·0.5H2O regulated by maleic acid from phosphogypsum: experimental and molecular dynamics simulation studies

Influence of crystal modifier on the preparation of α-hemihydrate gypsum from phosphogypsum

Experimental Study and Mechanism Analysis of Preparation of α-Calcium Sulfate Hemihydrate from FGD Gypsum with Dynamic Method

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Utilization of phosphogypsum to synthesize α-hemihydrate gypsum in H3PO4–H2O solution

Influence of crystal-transforming agent on the performance and mechanism of α-high-strength gypsum prepared from FGD gypsum

Effect of modifiers on crystalizing habit and mechanical strength of α-hemihydrate gypsum prepared from PG by an autoclaved method

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

The study on the effect of flotation purification on the performance of α-hemihydrate gypsum prepared from phosphogypsum

Study on Strengthening the Crystallization Process of Removing F and P from Phosphogypsum Produced by Dihydrate–Hemihydrate Wet Process

Impact of carboxylic acid structure on α-hemihydrate gypsum crystal morphology and mechanical strength

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions