Abstract:With the purpose to decrease the crystallinity of poly (e-caprolactone) (PCL), a small amount (8.5 mol%) of 2,2-dimethyltrimethylene carbonate (DTC) was added to copolymerize with epsilon-caprolactone (CL) using lanthanum tris (2, 6-di-tert-butyl-4-methylphenolate) (La(OAr)(3)) as catalyst. The produced polyester P(CL-co-DTC) (PCD) was well-characterized by H-1-NMR, SEC, DSC and WAXS. The results showed random copolymer PCD was synthesized. DSC and WAXS results proved PCD had a much lower crystallinity (chi(c) = 28.1%) compared to that of PCL (chi(c) = 44.7%). PCD, as well as PCL homopolymer containing 8 wt% salicylic acid as a model drug was electrospun into ultrafine fibers with the diameter around 1 mu m and further submitted to in vitro drug release test. The results showed that the PCD electrospun mat exhibited a controlled drug-release behavior while the PCL one displayed a burst-release behavior. The DSC and WAXS results showed PCL electrospun fibers had a much higher crystallinity (chi(c) = 79.3%) than that of PCD electrospun fibers (chi(c) = 40.3%) and this explained the difference of drug-release behaviors of the two electrospun mats. It was the non-crystalline domains involved in PCD that facilitated the compatibility between the polymer matrix and salicylic acid and allowed the drug to be released in a controlled way through the thermal motion of the polymer chain. This study provided a strategy for a better drug inclusion and release behavior by lowering the crystallinity of matrix material.

In-Situ Study on the Crystallizationof PCL Films Using FTIR

Effect of Crystallization Temperature on Crystal Modifications and Crystallization Kinetics of Poly(l‐lactide)

THE STUDY ON THE CRYSTAL MORPHOLOGY OF PCL THIN FILMS BY AFM

Crystalline Morphologies and Molecular Orientation of Poly(ε-caprolactone) Thin Films

In Situ FTIR and Generalized 2D IR Correlation Spectroscopic Studies on the Crystallization Behavior of Solution-Cast PHB Film

The Degree of Crystallinity Exhibiting a Spatial Distribution in Polymer Films

Crystallization Process of Poly(ɛ-Caprolactone)–poly(ethylene Oxide)–poly(ɛ-Caprolactone) Investigated by Infrared and Two-Dimensional Infrared Correlation Spectroscopy

Atr-Ftir Studies on the Effect of Thickness on the Crystallization of Poly(3-Hydroxybutyrate) Thin Films

Surface Crystal Nucleation and Growth in Poly (ε-caprolactone): Atomic Force Microscopy Combined with Fast Scanning Chip Calorimetry

In situ FTIR study on melting and crystallization of polyhydroxyalkanoates

CONTROLLED RELEASE OF SALICYLIC ACID FROM ELECTROSPUN MATS OF POLY(Ε-CAPROLACTONE) WITH LOW CRYSTALLINITY

Study on Solid Phase Crystallization of Silicon Films Deposited on Different Substrates

Influence of Freezing Layer on the Crystallization Kinetics of PCL on Oriented PE Film

Fourier-Transform Infrared Spectroscopic Studies Of Gelation And Crystallization Of Polystyrene Carbon-Disulfide Solutions

FT-IR Characterization of Liquid Crystalline Polymers

Study On Crystallization Kinetics Of Crosslinked Poly(Epsilon-Caprolactone)/Styrene-Acrylonitrile Copolymer Blends Prepared Through Irradiation By Electron Beam

Enhanced Crystallization of Bisphenol A Polycarbonate in Thin and Ultrathin Films by Supercritical Carbon Dioxide

Fourier transform infrared investigation on the interaction between CrCl3 and polyvinylpyrrolidone

Temperature-Variable FTIR and Solid-State 13C NMR Investigations on Crystalline Structure and Molecular Dynamics of Polymorphic Poly(l-lactide) and Poly(l-lactide)/Poly(d-lactide) Stereocomplex

A Study on the Epitaxial Ordering Process of the Polycaprolactone on the Highly Oriented Polyethylene Substrate

Crystallisation behaviours of ferroelectric P(VDF-TrFE) ultrathin films on different substrates