Abstract:Crystallization of poly(butylene terephthalate) (PBT) thin films from the glassy state has been investigated. The thin films on the silicon substrate with a thickness of no more than 300 nm were prepared by spin-casting and were examined by grazing-incidence X-ray scattering and atomic force microscopy before and after isothermal annealing at various temperatures (T(a)s). It is found that the virgin spin-cast thin films are anisotropic amorphous, with the PBT chains preferentially lying down on the substrate. The phase structure and morphology of the annealed thin films are strongly T-a-dependent. At T(a)s below 80 degrees C, the thin films remain amorphous due to the restricted chain segment mobility imposed by the one-dimensional (1D) confinement of the thin film. For T-a of 80-180 degrees C, isothermal annealing results in dominantly smectic nodules with a size of around 10 nm, which can be sustained regardless of extending the annealing time. When T-a is in the range of 180-200 degrees C, lath-like PBT crystals of alpha-form, which are edge-on lamellae, are observed to coexist with the smectic nodules. Further increasing T-a allows the lath-like crystals to grow substantially. However, owing to the high nucleation density, the crystals are small, showing a lateral size of just several dozens of nanometers. It is interesting to note that the 1D confinement condition could largely arrest the transformation from smectic-to-crystal over a wide temperature range, letting the smectic nodules survive at T-a below 200 degrees C. We further explored the interplay of smectic and crystal phases. It is unveiled that when the well-formed nodules are taken as the initial state for crystallization, the nodules can rapidly turn into nearly square-shaped crystal particles above 200 degrees C, which serve as the element blocks for the subsequent crystal growth. The combination of these blocks makes the lath-like crystals extend their lengths. Accordingly, we conjecture that when the PBT thin films are crystallized from the glassy state, there may exist a pathway of "glass-to-smectic-to-crystal".

Atr-Ftir Studies on the Effect of Thickness on the Crystallization of Poly(3-Hydroxybutyrate) Thin Films

Effects of Crystallization Temperature of Poly(vinylidene Fluoride) on Crystal Modification and Phase Transition of Poly(butylene Adipate) in Their Blends: a Novel Approach for Polymorphic Control.

Effect of Crystallization Temperature on Crystal Modifications and Crystallization Kinetics of Poly(l‐lactide)

Temperature‐dependent Polymorphic Crystalline Structure and Melting Behavior of Poly(butylene Adipate) Investigated by Time‐resolved FTIR Spectroscopy

Polymorphic Crystallization of Poly(Butylene Adipate) and Its Copolymer: Effect of Poly(Vinyl Alcohol)

The effect of polymer film thickness on the polymer crystallization restricted on substrate

A Grazing Incident Xrd Study on the Structure of Poly(3-Hydroxybutyrate) Ultrathin Films Sandwiched Between Si Wafers and Amorphous Polymers

In Situ FTIR and Generalized 2D IR Correlation Spectroscopic Studies on the Crystallization Behavior of Solution-Cast PHB Film

In situ FTIR study on melting and crystallization of polyhydroxyalkanoates

Studies on Pre-melting and Crystallization Process of Biosynthesized Poly(3-hydroxybutyrate) Using Two-dimensional Fourier-transform Infrared Spectroscopy

Effect of Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) on the Crystalline Properties of Poly(3-hydroxybutyrate-co-3-hydroxyvalerate)

THE STUDY ON THE CRYSTAL MORPHOLOGY OF PCL THIN FILMS BY AFM

Thickness-dependent Molecular Chain and Lamellar Crystal Orientation in Ultrathin Poly(di-N-hexylsilane) Films.

Thin-Film Crystallization of Poly(butylene Terephthalate) from the Anisotropic Amorphous State

In-Situ Study on the Crystallizationof PCL Films Using FTIR

Polymorphic Crystals from Different Thermal Treatments and Its Effect on Biodegradation Behavior of Poly(butylene Adipate)

Effects Of L-Phenylalanine As A Nucleation Agent On The Nonisothermal Crystallization, Melting Behavior, And Mechanical Properties Of Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate)

Crystalline Morphologies and Molecular Orientation of Poly(ε-caprolactone) Thin Films

Influence of film thickness on in vitro bioactivity of thin anatase films produced through direct deposition from an aqueous titanium tetrafluoride solution

AFM observation of sunflower like crystalline morphology formed in ultra thin film of poly (3 hydroxybutyrate co 3 hydroxyhexanoate)

Investigation of Water Diffusion in Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) by Generalized Two-Dimensional Correlation ATR–FTIR Spectroscopy