Abstract:In this study, we aimed to prepare and characterise hydrogel formulations using cellulose nanocrystals (CNCs), alginate (Alg), and polyethylene glycol diacrylate (PEGDA). The CNC/Alg/PEGDA formulations were formed using a double network crosslinking approach. Firstly, CNC was extracted from oil palm trunk, and the size and morphology of the CNCs were characterised using TEM analysis. Secondly, different formulations were prepared using CNCs, Alg, and PEGDA. The mixtures were crosslinked with Ca2+ ions and manually extruded using a syringe before being subjected to UV irradiation at 365 nm. The shear-thinning properties of the formulations were tested prior to any crosslinking, while the determination of storage and loss modulus was conducted post extrusion after the Ca2+ ion crosslink using a rheometer. For the analysis of swelling behaviour, the constructs treated with UV were immersed in PBS solution (pH 7.4) for 48 h. The morphology of the UV crosslinked construct was analysed using SEM imaging. The extracted CNC exhibited rod-like structures with an average diameter and length of around 7 ± 2.4 and 113 ± 20.7 nm, respectively. Almost all CNC/Alg/PEGDA formulations (pre-gel formulation) displayed shear-thinning behaviour with the power-law index η G′′) which suggests good shape fidelity. After the hydrogel constructs were subjected to UV treatment at 365 nm, only the F8 construct [4% CNC: 4% Alg: 40% PEGDA] demonstrated tough and flexible characteristics that possibly mimic the native articular cartilage property due to a similar water content percentage (79.5%). In addition, the small swelling ratio of 4.877 might contribute to a minimal change of the 3D construct’s geometry. The hydrogel revealed a rough and wavy surface, and the pore size ranged from 3 to 20 μm. Overall, the presence of CNCs in the double network hydrogel demonstrated importance and showed positive effects towards the fabrication of a potentially ideal 3D bioprinted scaffold.

Preparation of Calcium Alginate Hydrogel Based on Electro Induced Deposition Method

Hybrid 3D printing and electrodeposition approach for controllable 3D alginate hydrogel formation

Paper-Based Electrodeposition Chip for 3D Alginate Hydrogel Formation

Alginate Gel Electro-Writing for 3d Cell Printing

Dual Ionically Cross-linked Double-Network Hydrogels with High Strength, Toughness, Swelling Resistance, and Improved 3D Printing Processability

3D printed agar/ calcium alginate hydrogels with high shape fidelity and tailorable mechanical properties

Preparation, Mechanical and Biological Properties of Inkjet Printed Alginate/Gelatin Hydrogel

Coaxial Nozzle-Assisted 3D Bioprinting with Built-in Microchannels for Nutrients Delivery.

3D Printing Process for Hydro Gel with the Three-dimensional Micro Tubes to Mimic Vascular Network

Soft yet mechanically robust injectable alginate hydrogels with processing versatility based on alginate/hydroxyapatite hybridization

Preparation of Hollow Calcium Alginate Microfiber Composited with Silicon Dioxide

An integrated manufacturing strategy to fabricate delivery system using gelatin/alginate hybrid hydrogels: 3D printing and freeze-drying

Effect of Hydroxyapatite on the Preparation and Properties of Alginate Hydrogel

Microstructure and Properties of 3D Printed Agarose and Sodium Alginate Composite Hydrogel

Ionically crosslinked alginate hydrogels as scaffolds for tissue engineering: Part 1. Structure, gelation rate and mechanical properties

Comparative Study of Physicochemical Properties of Alginate Composite Hydrogels Prepared by the Physical Blending and Electrostatic Assembly Methods

Alginate gel electro-deposition for cell writing

Alginate-CaCO 3 hybrid colloidal hydrogel with tunable physicochemical properties for cell growth

Preparation and Characterisation of Cellulose Nanocrystal/Alginate/Polyethylene Glycol Diacrylate (CNC/Alg/PEGDA) Hydrogel Using Double Network Crosslinking Technique for Bioprinting Application

Shape-controlled Production of Alginate Hydrogel-Poly-l-lysine Microcapsules Based on Electrodeposition Method: Shape-controlled Microcapsules

4D Printing of a Sodium Alginate Hydrogel with Step-Wise Shape Deformation Based on Variation of Crosslinking Density