Abstract:Fe3O4 magnetic nanocrystals were prepared by coprecipitating Fe2+ and Fe3+ ions in an ammonia solution with ultrasonic enhancement and modification by the anionic surfactant sodium dodecyl sulfate (SDS). The product was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), high resolution transmission electron microscopy (HRTEM), N2 absorption-desorption, and thermogravimetric-differential scanning calorimetry (TG-DSC), respectively. The surface electrical properties and magnetic properties of the Fe3O4 magnetic nanocrystals were systematically investigated. The growth mechanism of the Fe3O4 magnetic nanocrystals was discussed. The results show that the Fe3O4 magnetic nanoparticles obtained are well-crystallized particles, with an average size of 10 nm, which have good dispersivity. The specific surface area of particles can reach as much as 91.6 m2 · g-1. The obtained nanoparticles also have good thermostability, and the isoelectric point (IEP) under water conditions is at pHpzc=5.7. Magnetic measurement reveals the magnetic nanoparticles are superparamagnetic with a saturation magnetization of 65.0 emu · g-1. The ultrasonic enhancement and the surfactant modification play an important role in the growth mechanism of the Fe3O4 superparamagnetic nanocrystals. These superparamagnetic nanocrystals might be applied to biological and medical fields such as cell or enzyme immobilization.

Research on Preparation of Paramagnetic Fe 3O4 Nanoparticles

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Preparation and Property Characterization of Fe3O4 Magnetic Nanoparticles

Synthesis and Magnetization Characteristics of Fe3O4 Nanoparticles

Preparation and Surface Modification of Magnetic Fe3O4 Nanoparticles

Synthesis and Characterization of Super-paramagnetic Fe3O4 Nanoparticles

Preparation of Fe3O4 superparamagnetic nanocrystals by coprecipitation with ultrasonic enhancement and their characterization

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Chemical Synthesis of Magnetic Fe<sub>3</sub>O<sub>4</sub> Nanoparticles

Preparation and Characterization of Fe 3 O 4 /ag Composite Magnetic Nanoparticles

Preparation and Magnetic Properties of Magnetic Magnetite Nano Particles

Preparation, Surface Functionalization and Application of Fe3O4 Magnetic Nanoparticles

Synthesis and characterization of magnetic nanometer pigment Fe3O4

Preparation and Characterization of Magnetic Nanoparticles of Fe-3 O-4 Coated with Mesoporous Sio2

Preparation of magnetic nanometer Fe3O4 with the method of complex compound-hydrolyzation deposition

Synthesis and Magnetic Properties of Fe3O4 Nanoparticles

Preparation of Fe 3 O 4 -Porphyrin Nano-Composited Particles and Their Optical and Magnetic Properties

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method

Selection of Preparation Conditions of Fe3O4 Magnetic Nanoparticles Based on Orthogonal Method

Research on the Preparation of Nano Materials Fe3O4

Synthesis and Magnetic Properties of Fe 3 O 4 Nanoparticles