Friction properties of orthodontic brackets coated with TiO2-xNy

Na Li,Hai-jing Zhou,Bing Han,Ying-jie Zhang,Bao-cheng Cao
DOI: https://doi.org/10.3969/j.issn.2095-4344.2014.47.014
2014-01-01
Abstract:BACKGROUND:In previous experiments, TiO2-xNy OBJECTIVE:To study the friction properties of orthodontic brackets coated with TiO-coated bracket has been confirmed to have excelent antibacterial properties and biological safety performance. 2-xNy METHODS: TiO film. 2-xNy film was prepared by radiofrequency magnetron sputtering on MBT bracket (0.022″). The TiO 2-x N y RESULTS AND CONCLUSION: TiO-coated brackets were analyzed by X-ray diffraction and scanning electron microscopy observations. The coefficient of static friction and coefficient of kinetic friction between the wires (0.012″, 0.014″, 0.016″) and orthodontic brackets were calculated. 2-xNy film on the bracket was of anatase structure, which was compact and had good crystalinity. Under dry condition, the coefficient of static friction and kinetic friction of the brackets coated with TiO2-xNy were less than those of ordinary brackets; under wet condition, the coefficients of static friction and kinetic friction of the brackets coated with TiO2-xNy were less than those of ordinary brackets, but the difference was not statisticaly significant. Nano-TiO2-xNy film can reduce the friction between bracket and archwire, which wil offer a novel opportunity to significantly reduce the friction during tooth movement.
What problem does this paper attempt to address?