Impacts of blade indentation on nickel-titanium file's fatigue fracture

Xiao-bo CHEN,Lin YUE,Xue-jun GAO

DOI: https://doi.org/10.3760/cma.j.issn.1002-0098.2012.s1.010

2012-01-01

Abstract:Objective To investigate impacts of the blade indentation of nickel-titanium files on the fatigue fracture.Methods A total of 216 used intact nickel-titanium files (HERO642,MicroMega,France,21 mm) were collected from the clinic.The surfaces were examined under stereomicroscope at 7 ×-45 × magnification.Any defect or distortion (plastic deformation) was recorded.From the 216,45 files with only planed cutting edges were randomly selected for further tests.Five new files of size 30 (taper 02) were selected as control group,Group 1.The 45 used files were divided into 3 groups,Group 2 planed files,Group 3 planed files with defected edge located at 3 mm from the end,and Group 4 planed files with defected edge located at 5 mm from the end.Cyclic fatigue tests were performed with a specific device which allowed the files to rotate freely inside a given curvature stainless steel tube.All files were rotated until fracture occurred.Time to fracture and length of fractured segment to the end were recorded.Results The 216 used nickel-titanium files were general intact observed by eyes.However,further inspected at 30 ×-45 × magnification,defects on the cutting edge were found in 26 files (12.0％).According to the cyclic fatigue test,the rotation fracture time (fatigue life) was found significantly less for the defected files compared with new files (one way ANOVA,P ＜ 0.01).All files were separated with a mean fracture length of 5-6 mm from the tip.Conclusions Blade indentation of nickel titanium files should be examined at above 30 × magnification for any fatigue defects.