Study of calcium carbonate eggshell powder for potential use as bone substitute

Shumin Wang,Ke Zhang,Liying Yu,Hongguo Zhou,Yatong Ding,Yida Cai

DOI: https://doi.org/10.11752/j.kqcl.2014.03.03

2014-01-01

Abstract:Objective To develop a new bone substitute derived from avian eggshell (ES) using micro-wave processing and observe its abilities of bone formation. Methods Calcium carbonate ES powder was pre-pared by microwave method with different heating time. The physicochemical characteristics of the new materials with or without microwave heating were analyzed by SEM、EDXA、XRD、FT-IR . A pilot animal study was conducted by creating standard defects of 5 mm diameter on parietal bone of New Zealand rabbits. The defects were filled with 60 min microwave heated ES powder whereas using microwave untreated ES powder and Bio-Oss in comparison. After 8 weeks new bone formation of defects were observed. Results SEM, XRD, FT-IR and EDXA analysis showed the micromorphology of the new materials turned from needle-like to ball-like structures as the microwave heating time prolonged. The characteristic peak of calcium carbonate was also increased at the same time. Carbon, phosphorus and calcium were confirmed in the new material as well. Animal study showed 5 mm defects on parietal bone filled with calcium carbonate ES powder had more calcified bone formation and less uncalcified new bone. Conclusions The study demonstrated the efficient use of microwave in converting ES powder from natural CaCO3 into calcium carbonate. The new material might be a potential bone substitute.