The preparation and application of calcium phosphate biomedical composites in filling of weight-bearing bone defects

Lijia Cheng,Tianchang Lin,Ahmad Taha Khalaf,Yamei Zhang,Hongyan He,Liming Yang,Shuo Yan,Jiang Zhu,Zheng Shi

DOI: https://doi.org/10.1038/s41598-021-83941-3

IF: 4.6

2021-02-19

Scientific Reports

Abstract:Abstract Nowadays, artificial bone materials have been widely applied in the filling of non-weight bearing bone defects, but scarcely ever in weight-bearing bone defects. This study aims to develop an artificial bone with excellent mechanical properties and good osteogenic capability. Firstly, the collagen-thermosensitive hydrogel-calcium phosphate (CTC) composites were prepared as follows: dissolving thermosensitive hydrogel at 4 °C, then mixing with type I collagen as well as tricalcium phosphate (CaP) powder, and moulding the composites at 37 °C. Next, the CTC composites were subjected to evaluate for their chemical composition, micro morphology, pore size, Shore durometer, porosity and water absorption ability. Following this, the CTC composites were implanted into the muscle of mice while the 70% hydroxyapatite/30% β-tricalcium phosphate (HA/TCP) biomaterials were set as the control group; 8 weeks later, the osteoinductive abilities of biomaterials were detected by histological staining. Finally, the CTC and HA/TCP biomaterials were used to fill the large segments of tibia defects in mice. The bone repairing and load-bearing abilities of materials were evaluated by histological staining, X-ray and micro-CT at week 8. Both the CTC and HA/TCP biomaterials could induce ectopic bone formation in mice; however, the CTC composites tended to produce larger areas of bone and bone marrow tissues than HA/TCP. Simultaneously, bone-repairing experiments showed that HA/TCP biomaterials were easily crushed or pushed out by new bone growth as the material has a poor hardness. In comparison, the CTC composites could be replaced gradually by newly formed bone and repair larger segments of bone defects. The CTC composites trialled in this study have better mechanical properties, osteoinductivity and weight-bearing capacity than HA/TCP. The CTC composites provide an experimental foundation for the synthesis of artificial bone and a new option for orthopedic patients.

multidisciplinary sciences

What problem does this paper attempt to address?

The paper aims to address the issue of filling materials for load-bearing bone defects. Currently, artificial bone materials are widely used for filling non-load-bearing bone defects, but they are rarely seen in the application of load-bearing bone defects. This is because the existing calcium phosphate (CaP) biomaterials, although well-applied in non-load-bearing bone defects, lack sufficient strength in load-bearing bone defects. Autologous bone grafting, while considered the gold standard for filling load-bearing bone defects, is limited in its application due to immune rejection and limited donor availability.

Therefore, the main goal of the research is to develop an artificial bone material with excellent mechanical properties and good osteogenic capability. To this end, researchers prepared collagen-thermosensitive hydrogel-calcium phosphate (CTC) composites and evaluated their chemical composition, microstructure, porosity, hardness, water absorption capacity, and osteoinductive ability through a series of experiments. Compared to traditional 70% hydroxyapatite/30% β-tricalcium phosphate (HA/TCP) biomaterials, CTC composites exhibited better mechanical properties, osteoinductivity, and load-bearing capacity. This indicates that CTC composites provide an experimental basis for synthetic artificial bone and offer a new option for orthopedic patients.