Abstract:The Chitosan/Hydroxyapatite/Snail-Shell/nano-Magnetite composite was used in this experiment to remove Zinc(II) and Cu(II) ions from the aqueous medium concurrently. A Central Composite Design, abbreviated as CCD, was used in order to find the optimal conditions for the independent variables. The first and second most important processes in this procedure were the synthesis of magnetite nanoparticles and the extraction of other components from brummagem materials, respectively. In the process of making the composite, the chitosan was first dissolved in acetic acid, and then the remaining components were added to the solution in the form of powder once the chitosan had been dissolved. An external magnet was used in conjunction with the nanoparticles that were embedded within the composites to remove the adsorbent from the solution. In order to describe the composite, EDX and SEM analyses were performed, and FAAS was employed in order to determine the number of ions that were still remaining throughout the solution after the analysis had been completed. Using CCD Expert Software, Zn(II) and Cu(II) concentration levels, the pH variables, contact time, and amount of adsorbent were modified to have values of 25.0 mg/L, 0.025 g, 5.5, 48.3 min, and 10.0 mg/L, respectively. These values represent the final results of the experiment. Several different models, including the Langmuir, Freundlich, and Tempkin models, were studied in order to analyze the data from the experimental isotherm models. In the cases of Cu(II) and Zn(II), respectively, the Freundlich and Langmuir models both revealed a reasonable level of fit. Four distinct classic kinetic models were applied in order to get an accurate match between the experimental findings at the starting concentration of ions and the predicted values. It was discovered that the pseudo-second-order model gives a suitable fit with the adsorption isotherms for both ions. This conclusion was reached on the basis of the observations.

The Preparation and Application for the Composite of Nanoscale Zero Valent Iron-Zeolite Adsorption to Cu2+ from Aqueous Solution

Zero-Valent Iron Nanoparticles (Nzvi) Supported By Kaolinite For Cu-Ii And Ni-Ii Ion Removal By Adsorption: Kinetics, Thermodynamics, And Mechanism

Removal of Uranium(vi) from Aqueous Solution Using Nanoscale Zero-Valent Iron Supported on Activated Charcoal

Carboxymethyl Chitosan-Fe3O4 Nanoparticles: Preparation and Adsorption Behavior Toward Zn2+ Ions

Zeolite-supported Nanoscale Zero-Valent Iron: New Findings on Simultaneous Adsorption of Cd(II), Pb(II), and As(III) in Aqueous Solution and Soil.

Efficient and selective removal of copper from aqueous solution by nanosized hydrated zirconium oxides loaded in vermiculite

[Removal of Antimony from Water by Nano Zero-Valent Iron/Activated Carbon Composites].

Synthesis and Characterization of Montmorillonite-Supported Zero-Valent Iron Nanoparticles with Application for Preconcentration of Zinc

Graphene Oxide-Supported Nanoscale Zero-Valent Iron Composites for the Removal of Atrazine from Aqueous Solution

Synthesis and characterization of zeolite-based composites functionalized with nanoscale zero-valent iron for removing arsenic in the presence of selenium from water

Removal of Hexavalent Chromium From Wastewater by Cu/Fe Bimetallic Nanoparticles

Adsorption-reduction strategy of U(VI) on NZVI-supported zeolite composites via batch, visual and XPS techniques

Synthesis of Nano‐zero‐valent Iron/Chitosan based on Bimetallic Nanoparticles for the Simultaneous Removal of Reactive Violet 5 and Reactive Blue 171 from Aquatic Media: Response Surface Methodology

Highly efficient adsorption and immobilization of U(VI) from aqueous solution by alkalized MXene-supported nanoscale zero-valent iron

Efficient adsorption and reduction of Cr(VI) and U(VI) by nanoscale zero-valent iron supported on polydopamine-decorated SBA-15

Zero Valent Iron Particles Impregnated Zeolite X Composites for Adsorption of Tetracycline in Aquatic Environment

Nanoscale Zero-Valent Iron (nzvi) Assembled on Magnetic Fe3O4/graphene for Chromium (VI) Removal from Aqueous Solution

Performance of lead ion removal by the three-dimensional carbon foam supported nanoscale zero-valent iron composite

Removal of Chromium (ⅵ)using Zero-Valent Nanoscale Iron Supported on Bentonite Enhanced by Cetyl-Trimethyl Ammonium Bromide

Synthesis of Na-A zeolite loaded bentonite and its application for removal of Cu(II) from aqueous solutions

Adsorption of zinc and copper ions simultaneously on a low-cost natural chitosan/hydroxyapatite/snail shell/nano-magnetite composite