Removal of Chromium (ⅵ)using Zero-Valent Nanoscale Iron Supported on Bentonite Enhanced by Cetyl-Trimethyl Ammonium Bromide

PENGXiuda,LIUHong,ZHOUYaduan,QINXiong,FENGTao

DOI: https://doi.org/10.7521/j.issn.0454-5648.2014.04.15

2014-01-01

Abstract:The nano-sized zero-valent iron supported on bentonite (B-nZVI)was prepared via surface modification technique u-sing cationic surfactant cetyl-trimethyl ammonium bromide (CTMAB).The nano-sized zero-valent iron particles of the modified product,marked as (B-nZVI)/CTMAB,appear dispersive and form chains on the surface of bentonite.The particles chains on the bentonite increase with the appropriate increase of CTMAB concentration.According to the Zeta potential measurement, the surface of 10-(B-nZVI)/CTMAB has greater positive charges than bare bentonite and B-nZVI.The Zeta potential of the former measured is 1.93 mV and the latter two are-2.52 mV and 0.54 mV,respectively.In addition,the specific surface area of (B-nZVI)/CTMAB is higher than that of B-nZVI due to the moderate existence of CTMAB.The increases of surface charge and specific surface area of 10-(B-nZVI)/CTMAB result in the increase of Cr(Ⅵ)removal efficiency,which is 33.7% greater than that of B-nZVI.The reaction of (B-nZVI)/CTMAB removing Cr(Ⅵ)follows the Langmuir-Hinshelwood model contai-ning two processes of adsorption and reduction.The proper addition of CTMAB can improve the reduction effect of the nano-sized zero-valent iron supported on bentonite.