Abstract:Nano zero-valent iron (Fe0, nZVI) has been extensively utilized in the treatment of dyed wastewater. However, the dispersibility, stability and reusability of nZVI need to be improved for both efficiency and environmental safety. One nZVI modified nanofiber composite membrane was successfully fabricated by electrospinning, and the performances in different catalytic systems were evaluated. The synthesized composite mat was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The loaded nZVI was verified by the change of fiber diameters and the distribution of iron element with/without loading. The composite membrane possessed good recyclability and dispersion property of nZVI with a mean diameter of 114.46 nm. Three Fenton-like oxidation systems (H2O2, Na2S2O8, and NaClO2) were selected and investigated for the degradation of Rhodamine B (RhB) in water using the as-prepared composite as a catalyzer. The degradability relationship of the oxidation systems was NaClO2>Na2S2O8>H2O2 with observed rate constants (Kobs) of 0.3155, 0.0547, and 0.014, respectively. 50 mg L−1 RhB was completely degraded by 1.5 mM NaClO2 in 15min, which is the best compared with the other two systems. The major free radical species (·OH, SO4·- and ClO2·) in the three oxidation systems were identified by electron paramagnetic resonance (EPR) and quenching studies. The degradation capacity could be maintained after five recycles and the leached nZVI from the composite was negligible (<0.55%). For the degradation process, the contribution of dark adsorption (Kads = 1.5489 × 10−3) was much smaller than that of natural-light-derived photocatalysis (Kphoto = 1.5489 × 10−3) with the adsorption capacity of 4.32 mg g−1 and oxidative degradation amounts of 9.46 mg g−1, 10.90 mg g−1 and 12.32 mg g−1 in H2O2, Na2S2O8 and NaClO2 systems, respectively. Our results demonstrated that the synthesized composite membrane demonstrated good catalytic properties with good recyclability and stability, and NaClO2 was the most efficacious system for RhB degradation in water.

Performance of lead ion removal by the three-dimensional carbon foam supported nanoscale zero-valent iron composite

Nanoscale Zero-Valent Iron Modified by Bentonite with Enhanced Cr(VI) Removal Efficiency, Improved Mobility, and Reduced Toxicity

Nano zero-valent iron loaded corn-straw biochar for efficient removal of hexavalent chromium: remediation performance and interfacial chemical behaviour

Research on Foam’s Carrying Capacity of Two Types of Nzvi

Removal of Chromium(VI) by Nanoscale Zero-Valent Iron Supported on Melamine Carbon Foam

Synergy of Carboxymethyl Cellulose Stabilized Nanoscale Zero-Valent Iron and Penicillium Oxalicum SL2 to Remediate Cr(VI) Contaminated Site Soil

Dual-supported nanoscale zero-valent iron for As(III) contaminated groundwater remediation

Nanoscale Zero-Valent Iron Dispersed by Sodium Alginate Enables Highly Efficient Removal of Lead (Pb) from Aqueous Solution

Removal mechanism of Pb(ii) from soil by biochar-supported nanoscale zero-valent iron composite materials

Integrated green complexing agent and biochar modified nano zero-valent iron for hexavalent chromium removal: A characterisation and performance study

Mediating the reactivity and selectivity of nanoscale zerovalent iron toward nitrobenzene under porous carbon confinement

Well-Dispersed Nanoscale Zero-Valent Iron Supported in Macroporous Silica Foams: Synthesis, Characterization, and Performance in Cr(VI) Removal

Nanoscale zero-valent iron loaded vermiform expanded graphite for the removal of Cr (VI) from aqueous solution

The high efficient Sb(III) removal by cauliflower like amorphous nanoscale zero-valent iron (A-nZVI)

Zeolite-supported Nanoscale Zero-Valent Iron: New Findings on Simultaneous Adsorption of Cd(II), Pb(II), and As(III) in Aqueous Solution and Soil.

Transport of nanoscale zero-valent iron in saturated porous media: Effects of grain size, surface metal oxides, and sulfidation

Calcium Hydroxide Coating on Highly Reactive Nanoscale Zero-Valent Iron for in Situ Remediation Application

Facile encapsulation of nano zero-valent iron with calcium carbonate: synthesis, characterization and application for iron remediation

Activated carbon fiber-supported nano zero-valent iron on Cr(VI) removal

Stabilization of nano zero-valent iron by electrospun composite mat with good catalysis and recyclability

Enhanced adsorption and reduction of Pb(II) and Zn(II) from mining wastewater by carbon@nano-zero-valent iron (C@nZVI) derived from biosynthesis