Abstract:A PLA-based bagasse cellulose composite material with excellent performance and low cost was prepared. As one of the most commonly used thermoplastic materials in fused deposition modeling (FDM), PLA is currently the most widely used three-dimensional (3D) printing technology. It has the natural advantage of being biodegradable. However, due to its poor toughness, it cannot meet the requirements for 3D printing consumables in some areas. Therefore, polylactic acid (PLA) is used as the matrix, tert-butyl peroxybenzoate (TBPB) are used as the free radical initiator, and glycidyl methacrylate (GMA) is used as the reaction monomer to prepare the PLAGMA graft product, which realizes the toughening of PLA, and the PLA/PLA-GMA/BC (bagasse cellulose) composite material is prepared by the physical blending method, which realizes the reinforcement of PLA; it was proved by fourier transform infrared spectroscopy (FTIR) and 1H NMR that GMA was successfully grafted onto the PLA molecular chain, and the influence of the grafting rate on the toughness of PLA-GMA was explored. It was concluded that the grafting rate of PLA-GMA with the best toughness was 10.33%. The strength is 15.94 MPa, the modulus of elasticity is 969.01 MPa, and the elongation at break is 278.17%, which is about 44 times the elongation at break of pure PLA. The PLA/PLA-GMA/BC composite material with high cellulose loading was prepared by physical blending. The effect of PLA-GMA content, BC particle size and BC content on the properties of composite materials was explored. The results showed that PLA-GMA when the addition amount is 25%, the capacity enhancement effect is the best; when the additional amount of BC is as high as 40%, the PLA/PLA-GMA/ BC composite still has good mechanical properties, and the addition of BC can promote the crystallization of PLA; DSC results show that BC can promote the crystallization of PLA, and the addition of PLA-GMA is not conducive to the composite material the formation of PLA crystalline regions; the temperature at the maximum decomposition rate of 40% BCB/25% PLA-GMA/PLA composite material is 355.44 celcius, and the thermal stability is improved. This study proves that the functional group properties of GMA realize the toughening and enhanced dual modification of polylactic acid, which expands the choice and application range of FDM 3D printing materials.

Plasticization of bamboo fiber/polylactic acid degradable composite

Toughness Enhancement of Poly(lactic Acid), Bamboo Particle and Ultrafine Bamboo-Char Ternary Biocomposites by Polyethylene Glycol Plasticization

Poly(Lactic Acid) Biocomposites Reinforced With Ultrafine Bamboo-Char: Morphology, Mechanical, Thermal, And Water Absorption Properties

Influence of Hot Press Molding Parameters on the Tensile Strength of Bamboo Fiber/PLA Composites

Preparation and Characterization of Three-Element Compound Plasticizing Bamboo Fiber-g-Polylactic Acid/Polylactic Acid Composite

Study on the Compatible Interface of Bamboo Fiber/polylactic Acid Composites by In-Situ Solid Phase Grafting

Preparation Of Plasticized Poly (Lactic Acid) And Its Influence On The Properties Of Composite Materials

Effect of plasticizer types on the properties of starch/polylactic acid composites

Mechanical and thermal properties of bamboo fiber reinforced polypropylene/polylactic acid composites for 3D printing

Influence of carboxy-terminated hyperbranched polyester and polyethylene glycol on the mechanical and thermal properties of polylactic acid/straw flour composites

Study on the Preparation and Properties of Bamboo Plastic Composites

Reinforcing the mechanical properties of bamboo fiber/low density polyethylene composites with modified bamboo-woven structure

Cardanol derivatives as compatibilizers for strengthening and toughening polylactic acid/bamboo fiber bio‐composites

Development of polylactic acid‐untreated bamboo filler composite and its chemical and mechanical properties

Preparation and Characterization of Polylactic Acid-G-bamboo Fiber Based on In-Situ Solid Phase Polymerization

Technology and Mechanism of Enhanced Compatibilization of Polylactic Acid-Grafted Glycidyl Methacrylate

Preparation and Characterization of Polylactic Acid/Bamboo Fiber Composites.

The combined plasticization of jute and tung oil anhydride for jute fiber reinforced poly(lactic acid) composites

Simultaneously Improving Toughness and Strength for Biodegradable Poly (lactic Acid) Modified by Rice Husk and Acetyl Tributyl Citrate

Poly (lactic Acid)/Wood Fibers Biodegradable Composites

Construction of high-performance and sustainable polylactic acid composites for 3D printing applications with plasticizer