Abstract:Different amounts of glyoxal and paraformaldehyde were used to synthesize phenol-glyoxal (PG) and phenol-paraformaldehyde (PPF) resins, which were compared with conventional phenol-formaldehyde (PF) resins. Glyoxal oxidation leads to a pH value of 9.83 for PG 2.2. With the addition of polyformaldehyde, PPF 2.2 exhibited the highest viscosity at 17333.33 mPa s. The PPF 2.0 plywood has a maximum bonding strength of 1.94 MPa. The formaldehyde emission of PG 1.8 plywood is found to have a minimum value of 0.025 mg/m 3 , reaching the E NF limit (≤0.025 mg/m 3 ). Acetaldehyde is found only in volatile organic compound (VOC) emissions from PG plywood and is associated with increased glyoxal. PPF plywood emitted more aromatic and total VOC (TVOC) than the other two plywood types. The measured TVOC for PPF 2.2 is 196.07 μg/m 3 . The results showed that the total cancer risk (TCR) values of PPF 1.8, PPF 2.0, and PG 1.8 were above the threshold of 1.00E-4, indicating a definite carcinogenic risk. Acetaldehyde in the PG plywood exceeded the safety threshold for noncarcinogenic risk. The use of paraformaldehyde in the wood-based panel production is been considered a possible means of improving the bonding strength of plywood. Glyoxal has also been shown to be a viable method for lowering the formaldehyde emissions from plywood. The VOC emissions from plywood changed significantly depending on the aldehyde used. Limiting VOCs that present high health hazards is crucial for reducing the negative impact of plywood on both indoor environments and human health.

The Effect of Formaldehyde- Emission Form Plywood of Poplar with Different Production Condition

Influencing factors analysis of formaldehyde emission from GluBam sheet by climate chamber test

Experimental Research on Formaldehyde Emission Characteristics from Glubam by Climate Chamber Test

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Comparison of the properties of phenolic resin synthesized from different aldehydes and evaluation of the release and health risks of VOCs

Formaldehyde Adsorption–Desorption of Poplar Bark

The Emission Characteristics of VOCs and Environmental Health Risk Assessment in the Plywood Manufacturing Industry: A Case Study in Shandong Province

Research Progress on Formaldehyde Emission of Wood-Based Panel

Study on formaldehyde and VOC emissions from different manufacturing stages of wood-based panels

The Removal of Formaldehyde from Urea Formaldehyde Adhesive by Sodium Borohydride Treatment and Its Application in Plywood

Different Test Methods on Formaldehyde Emission From Wood-Based Board

Study on the Release Law of Formaldehyde with Urea-formaldehyde Resin Adhesive Added to Attapulgite

Study on VOC Emissions from Plywood Using a Climate Chamber

Effect of Modification on Mechanical Property and Fire-Retardant Behavior of Fast-Growing Poplar Wood

Formaldehyde and VOC emissions at different manufacturing stages of wood-based panels

Research On The Application Of Tea And Waste Tea Products In Reducing Formaldehyde Of Particleboards

The effect of urea-formaldehyde adhesive modification with propylamine on the properties of manufactured plywood

Influence factors analysis of formaldehyde emission from wood-based panel by environmental chamber test and mathematical modeling

Characteristics of beech bark and its effect on properties of UF adhesive and on bonding strength and formaldehyde emission of plywood panels

The Effect of Heat Treatment and Acetylation on Formaldehyde Emission in Cellulose: A Molecular Dynamics Simulation Study

Influence of micron-sized oligomeric semisiloxane modification on surface properties of veneer and interfacial adhesion of EVA film/poplar plywood