The preparation and characterization of Fe3O4-layered double hydroxide composite and its application for the removal of Congo red

Bo ZHU,Yadong ZHANG,Jiangyan XU,Min CHEN,Ying SHI,Hongmei JIANG

DOI: https://doi.org/10.7685/jnau.201607004

2018-01-01

Abstract:[Objectives]In this paper,a new kind of Fe3O4-layered double hydroxide composite(MNP-LDH)was prepared by hydro-thermal method and it was used as adsorbent to remove Congo red in the aqueous solution.For comparison,the magnetic Fe3O4nano-particles(MNP)and Mg-Al hydrotalcite(LDH)were prepared in the same time. [Methods]The absorbents were characterized by scanning electron microscope(SEM),transmission electron microscope(TEM),fourier transform infraredspectroscopy(FT-IR),BET surface analyzer and X ray diffraction spectroscopy(XRD). The effects of pH,the initial concentration of Congo red and ultrasonic time on the adsorption rate of Congo red using static adsorption method were investigated in this study. The Congo red concentrations were determined using spectrophotometry.The Langmuir isotherm model was used for the isotherm study and the pseudo-second-order kinetic model was used to study the sorption kinetics. The desorption and regeneration of MNP-LDH was also evaluated. [Results] 1)From SEM and TEM,MNP-LDH and MNP were regular spherical structure and these particle sizes were both about 100 nm. The pore size of MNP-LDH was smaller than that of MNP. The peaks at 400-600 cm-1observed in infrared spectrums were related to Fe—O,Al—O and Mg—O,the peak at 1 300 cm-1was related to C—O and the peak at 3 400 cm-1was ascribed to O—H. The X-ray diffraction spectrum results showed that both materials had Fe3O4crystal and the characteristic peak of MNP-LDH was showed. The single point specific surface area of LDH was smaller than that of MNP-LDH.2)The adsorption capacity of Congo red decreased rapidly with the enhancing pH from 2 to 4 for MNP-LDH,MNP and LDH and then remained constant. The adsorption capacity of MNP-LDH was higher than that of MNP and LDH. 3)The adsorption capacity of MNP-LDH and MNP increased with the increasing of the initial concentration of Congo red. After the initial concentration reached 100 mg·L-1,the materials reached adsorption satura-tion. 4)The adsorption capacity of MNP-LDH increased with the increasing of the reaction time. After the reaction time reached 10 min,MNP-LDH reached adsorption equilibrium. 5)The experimental data fited well with the Langmuir adsorption isotherm and the pseudo-second-order kinetic model. 6)The effect of NaOH on desorption of Congo red was studied in this experiment. The spent MNP-LDH could be refreshed by 0.1 mol·L-1NaOH and it could be reused for four times without any decrease of desorption rate. 7)The prepared material was applied for the removal of Congo red and the recovery for the spiked industrial waste water sample was 113%,which indicated that the material in this work could remove Congo red from the water sample effectively. [Conclusions]The maximum adsorption capacity of MNP-LDH can be 265.96 mg·g-1when pH value is 2.5,reaction time is 15 min and the initial concentration of Congo red is 150 mg·L-1. Moreover,MNP-LDH has good reuse property,which displays that it is an excellent adsorption material.