Abstract:We conducted a shipboard ballast water test using seawater of extreme turbidity collected from Shanghai Port (China) (>300 mg total suspended solids (TSS)/L), and normal seawater collected in other ports (<100 mg TSS/L). All three types of International Maritime Organization (IMO)-approved ballast water management system (BWMS) tested failed to properly operate because of filter clogging or insufficient generation of oxidants under near-fresh water conditions with extremely high concentration of suspended solid during ballasting. It was also found that the number of microorganisms increased with longer ballast water retention time, with higher numbers in the treated discharge water. The results suggest that when operating a BWMS involving a filter unit in areas with water having high concentrations of suspended solids, the filter unit should be used during ballast water discharge, rather than during ballasting. This method has the advantage of removing ≥50 μm organisms at discharge that could not be removed by a filter during ballasting. For ballast water retained for long storage times, the results suggest the use of BWMSs involving UV units or electrolysis during deballasting. In addition, BWMSs involving electrolysis units provide the opportunity to maintain residual total residual oxidant (TRO) levels, using a partial ballast tank. Although the BWMSs tested are a small subset of the large number of IMO-approved BWMSs, the results demonstrate that there is a significant gap between the technology currently available and capacity to meet IMO and US Coast Guard standards.

Study on Effect of Metal Corrosion of Ballast Tank Caused by Ballast Water Treatment of Seawater Electrolysis

Experimental Study on Microbial Activity of Ship Ballast Water and Corrosion of Ballast Tank by Inert Flue Gas Deoxidation

Influence of Inactivation Treatment of Ship’s Ballast Water on Corrosion Resistance of Ship Steel Plate

A corrosion study of metals in the reclaimed water

Tests to Evaluate the Ecological Impact of Treated Ballast Water on Three Chinese Marine Species

Influence of Thermal Effect on Electrochemical Corrosion Behavior of T2 Copper in Simulated Seawater Environment

Experimental Study on Photocatalytic Treatment of Alien Organisms in Ship Ballast Water by F/Ce–TiO2

Effect of Electromagnetic Water Treatment on Water Environment and Metal Equipment

Study on corrosion behavior of typical carbon steel and low alloy steel in deep sea of different sea areas

Effect of sulphide in water on corrosion of copper alloys

Effects of Cu on Corrosion Resistance of Low Alloyed Steels in Acid Chloride Media

Effect of Reclaimed Wastewater Quality on Corrosion of Cooling Water Circulation System

Experimental Study on Compressive Property of Concrete Corroded by Seawater in Low-Temperate

Ballast Water Treatment Performance Evaluation under Real Changing Conditions

Corrosion Behavior of the Steel Used As a Huge Storage Tank in Seawater

The Effect of Immersion Corrosion Time on Electrochemical Corrosion Behavior and the Corrosion Mechanism of EH47 Ship Steel in Seawater

Model Tests for Corrosion Influence of Electrode Surface on Electroosmosis in Marine Sludge

Effect of Solution Treatment on Corrosion of GH4698 in Seawater

Study on the Initial Atmospheric Corrosion Behavior of Copper in Chloride-Containing Environments

Impacts of salinity stress induced by ballast water discharge on the ecosystem of shanghai port, China

Study on Corrosion Behavior of Copper-Clad Steel Bars with Unclad Two-End Faces for Grounding Grids in the Coastal Soil