On the Siding-rolling Friction and Wear Properties of Point Contact Friction Couple Between GCr15 Steel Ball and GCr15 Steel Disc

De-kun ZHANG,Jun-jie DUAN

DOI: https://doi.org/10.3969/j.issn.1674-358X.2014.04.002

2014-01-01

Abstract:A series of sliding‐rolling friction and wear experiments of a GCr15 steel ball against GCr15 steel plate under lubricated conditions were performed on NGY‐6 nano‐film thickness measuring instru‐ment .The effects of contact stress ,speed of steel ball and sliding‐rolling ratio on the friction coefficient and morphologies were investigated .The results showed that the friction coefficient increased with the increas‐ing of sliding‐rolling ratio ,and then reached a steady state at a fixed contact stress and speed of steel ball . As the sliding‐rolling ratio was fixed ,the friction coefficient increased gradually with the increasing of con‐tact stress .On the condition that the ball speed was lower than 300 r/min ,the friction coefficient decreased with the increasing of steel ball speed .When the steel ball speed and contact stress were over 300 r/min and 0 .84 GPa respectively ,the friction coefficient increased as the ball speed increased .Stribeck curve indi‐cated that the contact between the steel ball and plate was in hydrodynam lubrication regimes when the sliding‐rolling ratio was 0 .01 ;the lubrication condition transferred from boundary lubrication to mixed lu‐brication with the increasing of sommerfield parameter under the sliding‐rolling ratio of 0 .03 ;when the sliding‐rolling ratio were 0 .05 ,0 .1 ,0 .3 and 0 .5 respectively ,the contact was in conditions of boundary lu‐brication .As sliding‐rolling ratio was low ,the wear mechanism was mainly fatigue wear ,and with the slid‐ing‐rolling ratio increasing ,the wear mechanism changed to abrasive wear .