Modification and property analysis of nano-SiO2 and its composite electrolyte

Zhenxi WANG,Xin SHANG,Zhinong JIN,Guohua RAO,Qiulin OUYANG,Xiaohong LIU
DOI: https://doi.org/10.3969/j.issn.1006-4869.2015.04.002
2015-01-01
Abstract:Lithium ion battery,with the characteristics of high voltage,high capacity and high specific en-ergy,is an important energy storage device. The traditional liquid lithium ion battery is prone to the safety problems such as electrolyte leakage,explosion and short circuit. The polymer Li ion battery can solve the security problems well,but it also has such problems as lower conductivity,ion mobility fraction,and me-chanical properties. In this research,potassium tert butyl alcohol reacts with hydroxyl on the nano-SiO2 surface,then with 1,3-propylene sulfonic acid ester grafting. SiO2/P( MMA-S)composite electrolyte was prepared with modified or unmodified nano-SiO2 with styrene,methyl methacrylate. The results of FT-IR and TGA indicate that the surface of nano-SiO2 contains propylene sulfonic acid group. Meanwhile the morphology of the nano-SiO2 particles was studied by SEM,and the size distribution of the nanoparticles was uniform and the agglomeration was decreased after modification of the nano-SiO2 particles. Research on SiO2/P( MMA-S)composite polymer electrolyte results show that the modified nano-SiO2 composite e-lectrolyte membrane imbibition containing 6℅ quality rate could reach 310℅. After 15 days,the weight loss rate is no more than 18℅,the tensile strength could be more than 40. 0 MPa,and the elongation at break could be more than 40℅,with the ionic conductivity being up to 3 . 98 × 10-3 S/cm at room tempera-ture.
What problem does this paper attempt to address?