Synthesis and Morphology Control of Mesoporous Zr-SiO2 under Mildly Acidic Conditions

Zhengying WU,Wenjun ZHU,Yan LIN,Ruyu CUI,Chengbao LIU,Feng CHEN,Dongtian WANG,Zhigang CHEN,Xing ZHOU

DOI: https://doi.org/10.13801/j.cnki.fhclxb.20170216.001

2017-01-01

Abstract:It is not very easy to directly dope Zr into the mesoporous SiO2 .This is due to Zr species are generally difficult to co-condensation with siliceous species and then be co-incorporated into the framework of the SiO2 under strong acidic conditions.Therefore,a series of mesoporous Zr-SiO2 were successfully synthesized by a one-step method in the mildly acidic solutions that contain surfactant,hydrochloride acid,zinc acetate,siliceous and zirconi-um species.Experimental results show that all Zr-SiO2 samples synthesized with the Zr:Si molar ratio (r)equal to or less than 0.2:1 have the well-ordered mesostructures.The integrity of the mesostructure will decrease if further increase the r to 0.3 or 0.5.When the r in the initial reaction solution changes from 0.01 to 0.2,the cell parameter of the corresponding obtained material increases from 9.7 to 10.9 nm,and the wall thickness of the Zr-SiO2 sample also enlarges from 1.4 to 2.6 nm,respectively.This confirms that Zr species are incorporated into the framework of mesoporous SiO2 .The morphology of the Zr-SiO2 can be controlled by the incorporation of different amounts of Zr species.The highly regular fine particles with morphologies such as wormlike,grape-like and wheat grain-like are then obtained for the Zr-SiO2 samples.The mesoporous Zr-SiO2 materials present high adsorption abilities in the re-moval of methylene blue dye from aqueous solutions.