Influence of ammonium lignosulphonate on mechanical and thermal properties of polylactic acid/wood fiber biodegradable composites

HU Jianpeng,GUO Minghui

DOI: https://doi.org/10.13801/j.cnki.fhclxb.20140718.001

2015-01-01

Abstract:In order to investigate the feasibility of biomass resources improving the interface and comprehensive properties of bio-composites,the oxidation modification ammonium lignosulphonate(OMAL)was used to produce the environment friendly OMAL-polylactic acid(PLA)/wood fiber(WF)composites by the high speed mix-flat hot pressing process with WF as matrix and PLA as reinforcement.The influence of OMAL on mechanical and thermal properties of OMAL-PLA/WF composites was investigated.The results show that OMAL can improve the modulus of rupture,elastic modulus and internal bond strength of OMAL-PLA/WF composites with mass ratio 7∶3of WF to PLA,and the optimized mechanical properties are achieved with OMAL dosage of 15wt%-20wt%.When the OMAL dosage is 20wt%,the thermal decomposition initial temperature decreases 45 ℃,the characteristic peak of thermal decomposition rate arises 107 ℃in advance,the residue quantity increases by 5.3%,the glass transition temperature,cold crystallization temperature and melting temperature shift to low temperature,the storage modulus and loss tangent increase with the temperature range of the platform stage increases about 20℃compared to that of PLA/WF composites.