Abstract:The aim of this study was to investigate the physical, mechanical, morphological, structural, and thermal properties of polylactic acid (PLA) and polyhydroxybutyrate (PHB) biopolymer composites reinforced with thermally treated wood flour and to determine the formulations having optimum properties by using multi-criteria decision-making (MCDM) methods. As a filler, Scots pine wood flour (untreated and thermally treated at 212 °C) was used at the loading rates of 10% and 30%. The samples were prepared using a twin-screw extruder and then by compression molding. The results showed that the addition of both thermally treated and untreated wood flour slightly increased the density of the composites. According to the color measurement, the thermally treated wood composites were slightly darkened in appearance. In the composites, with both wood fillers, the water absorption and thickness swelling ratios had increased during the 20–250 days of water exposure. Lower water absorption and thickness swelling rates were found for the composites with thermally treated wood filler compared to the other composites. The wood fillers generally lowered the mechanical properties of the PLA and PLA/PHB composites, with the PHB composites as the exception. However, the tensile modulus and Izod impact strength of the composites generally increased with the addition of wood fillers. Morphological examination performed by scanning electron microscopy (SEM) indicated that the wood flour was mostly homogeneously distributed in the matrix, which improved the mechanical properties of the composites. Thermogravimetric analysis (TGA) showed that the addition of wood filler to the neat biopolymers as a rule did not provide significant improvement in the thermal stability; however, the fillers increased the thermal stability of neat PHB. The Fourier-transform infrared (FTIR) spectroscopy detected no differences in the chemical structure of the composites. The X-ray diffraction (XRD) results indicated a general increase in the crystallinity with the addition of wood fillers to the neat biopolymers and the blends. All the findings were subjected to MCDM analysis to determine the formulation having the optimum properties and the results showed this to be the neat PLA sample.

Effect of oxidized wood flour as functional filler on the mechanical, thermal and flame-retardant properties of polylactide biocomposites

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Intumescent-Grafted Bamboo Charcoal: A Natural Nontoxic Fire-Retardant Filler for Polylactic Acid (PLA) Composites

Development of Biodegradable Flame-Retardant Bamboo Charcoal Composites, Part I: Thermal and Elemental Analyses.

Combination of Corn Pith Fiber and Biobased Flame Retardant: A Novel Method toward Flame Retardancy, Thermal Stability, and Mechanical Properties of Polylactide

Development Of Biodegradable Flame-Retardant Bamboo Charcoal Composites, Part Ii: Thermal Degradation, Gas Phase, And Elemental Analyses

Multifunctional lignin-poly (lactic acid) biocomposites for packaging applications

Improved Mechanical Properties and Flame Retardancy of Wood/PLA All‐Degradable Biocomposites with Novel Lignin‐Based Flame Retardant and TGIC

Enhancement of Flame Retardancy and Mechanical Properties of Polylactic Acid with a Biodegradable Fire-Retardant Filler System Based on Bamboo Charcoal

Construction of polylactic acid-based flame retardant composites by zinc oxide and bamboo carbon

Fire Retardancy, Water Absorption, and Viscoelasticity of Borated Wood—Polycarbonate Biocomposites

Wood flour and hazelnut shells polylactide‐based biocomposites for packaging applications: Characterization, photo‐oxidation, and compost burial degradation

Thermal Degradation and Flame Retardance of Biobased Polylactide Composites Based on Aluminum Hypophosphite

Influence of a Biofiller, Polylactide, on the General Characteristics of Epoxy-Based Materials

A Polyphosphoramide-Grafted Lignin Enabled Thermostable and Fire-Retardant Polylactide with Preserved Mechanical Properties

The Influence of Urtica dioica and Vitis vinifera Fibers on the Thermal Properties and Flammability of Polylactide Composites

Influence of Newly Organosolv Lignin-Based Interface Modifier on Mechanical and Thermal Properties, and Enzymatic Degradation of Polylactic Acid/Chitosan Biocomposites

Effect of wood flour and compatibilizer content on the properties of wood-plastic composites

Effects of Wood Content and Modification on Properties of Wood Flour/Polybutylene Adipate Terephthalate Biocomposites

Synergistic reinforcement of polylactic acid/wood fiber composites by cellulase and reactive extrusion

Ultra-light polylactic acid/combination composite foam: A fully biodegradable flame retardant material