Effect of Ni interlayer on the mechanical properties of laser spot welded joints of QBe2.5/20#steel

Jinrong MAO,Yongde HUANG,Lili REN,Jilin XIE,Peng HE

DOI: https://doi.org/10.11951/j.issn.1005-0299.20160042

2017-01-01

Abstract:Flow valve precision often uses beryllium bronze/steel composite components. In this paper, to optimize the mechanical properties of the lap joints between QBe2.5 and 20# steel, 0.05 mm-thick pure Ni is adopted as an interlayer for laser micro spot welding. The weld formation, mechanical properties and element distribution of the joints with and without Ni interlayer are contrastively analyzed through optical microscopy ( OM) , tensile shear test, microhardness tester and energy spectrum analysis( EDS) . The results showed that the tensile shear of the joint with Ni interlayer increased by 61. 5%, weld penetration decreased and did not appear to collapse basically compared with the joint without Ni interlayer. Fe content inceresed, and Cu content decreased and enhanced the joint with Ni interlayer toughness. The microhardness value increased gradually along the depth direction of the weld after joining the Ni interlayer. However, the microhardness of joint without Ni interlayer was unchanged. And the average microhardness value at the joint interface was low obviously compared with the joint with Ni interlayer. Ni interlayer materials can significantly improve the weld fusion ratio and improve the shear strength, ductility and toughness of the joints.