Effect of the Welding Position on Weld Quality when Laser Welding Inconel 617 Ni-based Superalloy

Hao Cheng,Li Kang,Jincheng Pang,Boce Xue,Dong Du,Baohua Chang

DOI: https://doi.org/10.1016/j.optlastec.2021.106962

2021-01-01

Abstract:Inconel 617 Ni-based superalloy sheets were joined using a laser-welding process. The welding experiments were conducted on four different welding positions (i.e., flat, horizontal, vertical-up, and vertical-down), using two sets of welding parameters with different heat inputs. Then, the geometry, internal defects, mechanical properties, and molten-pool dynamics of the laser joints were evaluated. The results showed that, when using high heat input parameters, the welding position has an obvious effect on the laser weld quality. The top surface of the flat weld and the root surface of the vertical-down weld are both slightly concave. Moreover, the horizontal weld and vertical-down weld have serious keyhole-induced porosity defects, which lead to relatively worse mechanical properties. The analysis shows that the stability of keyhole differs for different welding positions; keyhole-induced porosity is easily generated in the horizontal and vertical-down positions. Moreover, solid metal blocks escape routes of the bubbles, resulting in more serious porosity for these welding positions. However, when using low-heat input parameters, the welding position has less influence on the laser weld quality because there is less molten metal, which makes the keyhole more stable in different welding positions.