Preparation of Silica Membrane by So-l gel Method and Its Performances

Yingchun ZHANG,Ling WENG,Xiaorui ZHANG
2017-01-01
Abstract:Silica sol was prepared by sol-gel method with TEOS as precursor and nitric acid as catalyst.The silicon dioxide film was prepared by heat treating the silica film which was coated on the metal surface by the pulling method. The hydrophobic property of the film was improved by adding F-silane coupling agent into the sol.The chemical composition,micro morphology and thermal stability of the thin films were analyzed by FT-IR,SEM and TG,respectively.The effects of different raw material ratio and film forming temperature on the hardness,adhesion and corrosion resistance of the films were studied.Results show that when in the molar ratio of silicic and acid is 1 5:1,the hardness of silica film reach the highest value,which is up to 9 H;the silica film also has the best adhesion performance (up to 2),the longest salt fog time (25 min)and the best salt fog corrosion resistance performance. SEM analysis indicates that the surface cracks of the films are minimal and no obvious gel precipitates;TG analysis shows that the reaction temperature has little influence on the thermal stability of films.
What problem does this paper attempt to address?